The invention discloses a new preparation method of non-woven wallpaper, which comprises the following steps: (1) fiber ratio: beating bleached chemical pulp to the beating degree of 18 28 SR and adding chemical additives to the blended fibers; (2) making: making base paper from the blended fibers containing chemical additives through long mesh or inclined mesh or circular mesh paper machine; (3) coating: color coating; Material, chemical additives and adhesives are mixed to form coating solution, and the base paper is coated by air knife and scraper inside or outside the machine; (4) finishing process: the coated base paper is dried and hot-pressed by calender; (5) coiling product: the finished base paper is rolled into base paper. The non-woven wallpaper prepared by the invention has high smoothness, natural texture of fibers on the non-coated surface, strong stereoscopic sense and convenient secondary construction.
【技术实现步骤摘要】
一种新型无纺壁纸的制备方法
本专利技术属于壁纸
，具体涉及一种新型无纺壁纸的制备方法。
技术介绍
目前市场上主要以普通PVC壁纸和无纺壁纸为主，其中PVC壁纸因花色多样、价格适宜、耐刮擦性能好、加工方式多样等优点而应用最为广泛，但是其在加工或者使用过程会存在与基纸结合力差易产生分层，硬挺的纤维易在涂布过程中形成泡点、强度较差、伸缩变形大等缺点；近年来无纺壁纸逐渐流行起来，具有色彩丰富、装饰效果高贵典雅等特点外，还具有成纸强度高、伸缩变形小、可直接印刷等优点，因此越来越受到市场的欢迎，但是其由于表面粗糙、高透气性、孔隙较多无法进行PVC涂布，后续发泡压花也无法进行，加工方式相对比较单一，产品特色不强。
技术实现思路
本专利技术针对现有技术的状况，克服上述缺陷，提供一种新型无纺壁纸的制备方法。本专利技术采用以下技术方案，所述一种新型无纺壁纸的制备方法，包括如下步骤：(1)纤维配比：将漂白化学浆打浆至18-28°SR的打浆度并与，在混合的纤维中加入化学添加剂；(2)抄造：将所述含有化学添加剂的混合纤维经长网或者斜网或者圆网纸机抄造得原纸基纸；(3)涂布：将颜料、化学添...
【技术保护点】
1.一种新型无纺壁纸的制备方法，其特征在于，包括如下步骤：(1)纤维配比：将漂白化学浆打浆至18‑28°SR的打浆度并与，在混合的纤维中加入化学添加剂；(2)抄造：将所述含有化学添加剂的混合纤维经长网或者斜网或者圆网纸机抄造得原纸基纸；(3)涂布：将颜料、化学添加剂与胶黏剂混合成为涂布液，将原纸基纸采用机内或者机外气刀、刮刀等涂布方式进行涂布；(4)整饰加工：将涂布的原纸经干燥并采用压光机热压方式进行表面整饰；(5)卷取成品：将整饰加工好的原纸卷取成为原纸成纸。
【技术特征摘要】
1.一种新型无纺壁纸的制备方法，其特征在于，包括如下步骤：(1)纤维配比：将漂白化学浆打浆至18-28°SR的打浆度并与，在混合的纤维中加入化学添加剂；(2)抄造：将所述含有化学添加剂的混合纤维经长网或者斜网或者圆网纸机抄造得原纸基纸；(3)涂布：将颜料、化学添加剂与胶黏剂混合成为涂布液，将原纸基纸采用...
【专利技术属性】
技术研发人员：卢福全，
申请(专利权)人：浙江丰舟特种纸有限公司，
类型：发明
国别省市：浙江,33