The invention provides a preparation method of nylon wool, which comprises the following steps: (1) weighing 85 95% polyester and 5 15% nano-calcium carbonate by weight percentage and blending; (2) drawing the mixture of polyester and nano-calcium carbonate; (3) acid treatment of the drawn silk to obtain the nylon wool; and also providing a preparation method of makeup brush wool. One end of dragon hair is immersed in cellulose oxidizer, the oxidation time is controlled according to the length of the hair peak, grinding, washing and drying are carried out, and cosmetic brush hair is obtained. The nylon hair of the invention has great toughness, strong dipping power, even dipping powder, and can save powder consumption.
【技术实现步骤摘要】
一种尼龙毛的制备方法
本专利技术属于高分子材料
，特别是涉及一种尼龙毛的制备方法。
技术介绍
化妆刷主要用于彩妆等领域，一般可以分为蜜粉刷、腮红刷、眉刷、眼影刷、眼线刷、睫毛刷等，但不同化妆刷的结构却大都类似。化妆刷主要由两部分构成，即为柄端和刷毛。传统化妆刷的制造材料，柄端主要使用木质或者有机合成材料；刷毛主要使用天然动物体毛或者人造尼龙毛等合成材料。刷毛的材质决定了化妆刷的质量和价格。通常，动物毛比合成尼龙毛触感好，上妆效果也更服帖，但动物毛往往成本较高，有异味，颜色单一，受养殖户自然产量的限制，同时涉及到动物保护等伦理道德方面的内容。而目前市面上的合成尼龙毛在上粉性能方面有所不足，例如蘸粉力比较差，粘粉不均匀，上妆服帖度不足，同时部分使用者会出现易过敏的现象。近年来，有序多孔材料研究领域获得了飞速的发展，多孔材料具有超高的比表面积、均一的孔形、孔径及均匀的有序排列，使其对被处理分子的尺寸和形状具有良好的选择性，在催化、分离、光学、纳米材料、微器件和传感器等方面显示出巨大的应用潜力。将有序多孔材料的制作原理运用到尼龙毛的生产上面，通过对传统聚酯尼龙毛表面...
【技术保护点】
1.一种尼龙毛的制备方法，其特征在于，包括以下步骤：(1)按重量百分比计，称取85‑95％的聚酯和5‑15％的无机盐，混和均匀；(2)将聚酯和无机盐混合物进行拉丝；(3)将经过步骤(2)拉出的丝进行酸处理，得到所述尼龙毛。
【技术特征摘要】
1.一种尼龙毛的制备方法，其特征在于，包括以下步骤：(1)按重量百分比计，称取85-95％的聚酯和5-15％的无机盐，混和均匀；(2)将聚酯和无机盐混合物进行拉丝；(3)将经过步骤(2)拉出的丝进行酸处理，得到所述尼龙毛。2.根据权利要求1所述的尼龙毛的制备方法，其特征在于，所述聚酯为聚对苯二甲酸乙二醇酯、聚对苯二甲酸丙二醇酯或聚对苯二甲酸丁二醇酯。3.根据权利要求1所述的尼龙毛的制备方法，其特征在于，所述无机盐为碳酸钙、碳酸镁和碳酸钠中的一种或多种。4.根据权利要求3所述的尼龙毛的制备方法，其特征在于，所述无机盐为碳酸钙，其中所述碳酸钙为纳米级碳酸钙，其粒径为0.03um-1um。5.根据权利要求4所述的尼龙毛的制备方法，其特征在于，所述纳米级碳...
【专利技术属性】
技术研发人员：王春波，魏志军，陈经尚，陈志强，张晓红，张洁梅，陈嘉迎，蔡颜娟，
申请(专利权)人：中山尚洋科技股份有限公司，
类型：发明
国别省市：广东,44