The invention discloses a heat treatment method of GT35 steel bonded cemented carbide. GT35 steel bonded cemented carbide is composed of CrMo low alloy steel as bonding phase and TiC particles with mass fraction of 35% as hard phase. GT35 cemented carbide with stable structure and low residual stress was obtained by austenitizing, quenching, isothermal tempering and combined heat treatment of cold and hot cycles. The GT35 steel-bonded cemented carbide with the heat treatment method of the invention reduces the residual stress on the surface of the cemented carbide and improves the hardness of the alloy compared with the alloy obtained by the conventional treatment method, and the size change is less than 0.2 after being placed at room temperature for half a year.
【技术实现步骤摘要】
一种GT35钢结硬质合金的热处理方法
本专利技术涉及一种GT35钢结硬质合金的热处理工艺，属于复合材料热处理加工
技术介绍
GT35钢结硬质合金具有硬度高、耐磨性好、机加工性能优良等特点，已经广泛应用于航天航空、汽车工业以及工模具等领域，GT35钢结硬质合金是以CrMo低合金钢为粘结相，质量分数为35%的TiC颗粒为硬质相组成。在航天航空应用领域，GT35材料用于制造惯性制导系统中动压气浮轴承陀螺马达的轴、止推板等重要部件；零部件的微小变化均可能降低器件的可靠性，甚至影响整个惯性系统的运行稳定性。在工模具应用领域，模具材料的变形也会在一定程度上影响产品的质量，降低模具的使用精度和寿命。GT35材料的尺寸稳定性主要受两个方面的影响：一是由于材料在制备与服役过程中基体相易发生马氏体相变、残余奥氏体分解、碳化物析出等组织结构变化。在这些相转变过程中，由于各相比体积的差异，从显微组织稳定性方面影响了材料的尺寸稳定性；二是由于材料在制备、加工及热处理过程中会产生宏观残余应力及微观应力，在长期存放或服役过程中，会发生应力松弛与释放行为，从而降低材料的尺寸稳定性。因而...
【技术保护点】
1.一种GT35钢结硬质合金的热处理方法，其特征在于，包括以下步骤：1）、对锻造态的GT35钢结硬质合金进行奥氏体化处理；2）、对经过步骤1）处理后的GT35钢结硬质合金进行淬火处理；3）、对经过步骤2）处理后的GT35钢结硬质合金进行等温回火处理；4）、对经过步骤3）处理后的GT35钢结硬质合金进行冷热循环处理。
【技术特征摘要】
1.一种GT35钢结硬质合金的热处理方法，其特征在于，包括以下步骤：1）、对锻造态的GT35钢结硬质合金进行奥氏体化处理；2）、对经过步骤1）处理后的GT35钢结硬质合金进行淬火处理；3）、对经过步骤2）处理后的GT35钢结硬质合金进行等温回火处理；4）、对经过步骤3）处理后的GT35钢结硬质合金进行冷热循环处理。2.根据权利要求1所述的一种GT35钢结硬质合金的热处理方法，其特征在于，所述奥氏体化处理工艺为：将锻造态的GT35钢结硬质合金加热至800~1100℃，保温20~100min。3.根据权利要求1所述的一种GT35钢结硬质合金的热处理方法，其特征在于，所述淬火处理工艺为：将奥氏体化处理后的GT35钢结硬质合金进行油淬处理，油温为20~40℃，淬火试样与淬火介质的质量比为1:30到1:35，淬火时间为5~10min。4...
【专利技术属性】
技术研发人员：肖来荣，涂晓萱，赵小军，蔡圳阳，宋宇峰，韦道明，曾德露，
申请(专利权)人：中南大学，
类型：发明
国别省市：湖南,43
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。