The invention discloses a water-borne wall coating and a preparation method thereof. The waterborne wall coating contains the following weight components: silicone acrylic emulsion 30, 40 titanium dioxide, 15, 25, cordierite 20, 30, nano zirconia 10, 15 hollow glass beads 5, 15 talcum powder 2, 2 sericite powder, 2 water glass, ultraviolet ray absorbents, UV Absorbents, film forming auxiliaries, dispersing agents, dispersing agents, wetting agents, and defoamer. Thickening agent 3 5 anti-mildew agent 0.1 0.3 water 15 20. The beneficial effect of the invention is that the waterborne wall coating has excellent thermal insulation performance, thereby realizing external thermal insulation of the external wall and reducing energy consumption.
【技术实现步骤摘要】
水性墙体涂料及其制备方法
本专利技术涉及墙体涂料，特别涉及一种水性墙体涂料及其制备方法。
技术介绍
墙体涂料是指用于对建筑墙体起装饰和保护，使建筑墙体美观整洁，同时也能够起到保护建筑墙体，延长其使用寿命的作用的涂料。墙体涂料按建筑墙体分类包括内墙涂料和外墙涂料两大部分。内墙涂料注重装饰和环保；外墙涂料注重防护和耐久。公开号为CN105400352A的中国专利公开了一种高耐候水性墙体涂料及其制备方法。该水性墙体涂料按重量份数计，由以下组份制成：纯丙乳液30～38份，PEVE乳液18～24份，CPVC8～10份，颜料4～6份，填料10～16份，水15～21份，润湿剂0.2～0.4份，分散剂0.2～0.5份，成膜助剂2～2.5份，增稠剂0.1～0.6份，防霉剂0.1～0.3份，乙二醇0.5～0.6份，掺铝氧化锌9～14份。该水性墙体涂料具有良好的耐臭氧老化性和红外反射性能，可达到很好的耐候效果，能够满足外墙涂料的防护和耐久要求。目前，外墙外保温是最有效的建筑节能方式，而外墙涂料是实现外墙外保温的重要发展方向。但是，上述水性墙体涂料的保温性能不佳，有待改进。
技术实现思路
本...
【技术保护点】
1.一种水性墙体涂料，其特征是：包括如下重量份数的组分：硅丙乳液 30‑40份钛白粉 15‑25份堇青石 20‑30份纳米氧化锆 10‑15份空心玻璃微珠 5‑15份滑石粉 2‑4份绢云母粉 2‑4份水玻璃 10‑15份紫外线吸收剂 0.5‑1份成膜助剂 0.5‑1份分散剂 0.5‑1份润湿剂 0.5‑1份消泡剂 0.1‑0.5份流平剂 0.5‑1份增稠剂 3‑5份防霉剂 0.1‑0.3份水 15‑20份。
【技术特征摘要】
1.一种水性墙体涂料，其特征是：包括如下重量份数的组分：硅丙乳液30-40份钛白粉15-25份堇青石20-30份纳米氧化锆10-15份空心玻璃微珠5-15份滑石粉2-4份绢云母粉2-4份水玻璃10-15份紫外线吸收剂0.5-1份成膜助剂0.5-1份分散剂0.5-1份润湿剂0.5-1份消泡剂0.1-0.5份流平剂0.5-1份增稠剂3-5份防霉剂0.1-0.3份水15-20份。2.根据权利要求1所述的水性墙体涂料，其特征是：所述钛白粉为金刚石型钛白粉。3.根据权利要求1所述的水性墙体涂料，其特征是：所述紫外线吸收剂选用苯并三唑。4.根据权利要求1所述的水性墙体涂料，其特征是：所述成膜助剂为十二酯醇，所述分散剂为聚丙烯酸钠，所述润湿剂为司盘80，所述消泡剂为乙二醇硅氧烷，所述流平剂为聚二甲基硅氧烷，所述增稠剂为羟甲基纤维素钠。5.根据权利要求1所述的水性墙体涂料，其特征是：所述防霉剂为ActicideEPW。6.根...
【专利技术属性】
技术研发人员：曹德斌，
申请(专利权)人：浙江纺织服装职业技术学院，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。