The invention discloses a waterborne road marking paint, which is characterized by weight percentage, comprising the following components: polyester compound acrylic emulsion 15, 20%, glass beads 25, 28%, titanium white powder 15, 20%, talcum powder 12 12 15%, anti settling agent 1 1 2%, antifreeze agent 0.5 0.5, dispersant agent 2%, wetting agent, pH, and defoaming agent. 0.2 0.6% preservative, 0.2 0.5% thickener and 20 25% water. The waterborne road marking paint of the invention has excellent abrasion resistance, water resistance, wide adhesion, and high refractive index glass beads have obvious reflective warning effect, and is suitable for road marking such as asphalt or cement concrete.
【技术实现步骤摘要】
一种水性马路划线漆及其制备方法
本专利技术涉及涂料
，特别是涉及一种水性马路划线漆及其制备方法。
技术介绍
目前，我国划线漆涂料以C5石油树脂及松香改性的树脂为基料的热熔型和以聚丙烯酸酯树脂为基料的常温溶剂型为主。随着时代的发展，科技的进步，此类涂料类型由单一的常温溶剂型发展成为常温溶剂型、加热溶剂型、热熔型及环保型涂料。热熔型涂料存在施工速度慢、施工条件差、改线困难等缺点，溶剂型涂料含有大量挥发性有机物(VOC)，当漆膜干燥过程中，对周围环境造成很大的污染及危害，不符合环保的要求。而环氧地坪涂料的无溶剂化主要采用反应性活性稀释剂代替非活性稀释剂来实现，非活性稀释剂不能与环氧树脂及固化剂进行反应，它在配方中纯属物理混入过程；用量少时对涂膜物理性能几乎无影响，但对涂膜的耐化学药品性有不利的影响；用量大时会降低涂膜物理性能，特别是由于非活性稀释剂逸出挥发，会引起涂膜收缩性增加和粘接力下降。活性稀释剂本身粘度低，含有环氧基，能与胺固化剂反应进入涂膜的微观结构中，若用量合适，即可降低涂料粘度满足作业要求，又可保证涂膜的力学性能和耐化学性。然而，无溶剂环氧涂料中的活性...
【技术保护点】
1.一种水性马路划线漆，其特征在于：按重量百分比计，包括以下组分：聚酯复合丙烯酸乳液15‑20％，玻璃珠25‑28％，钛白粉15‑20％，滑石粉12‑15％，防沉剂1‑2％，防冻剂0.5‑1％，分散剂0.5‑0.8％，润湿剂0.1‑0.2％，消泡剂0.3‑0.5％，pH调节剂0.2‑0.3％，防腐剂0.2‑0.6％，增稠剂0.2‑0.5％，水20‑25％。
【技术特征摘要】
1.一种水性马路划线漆，其特征在于：按重量百分比计，包括以下组分：聚酯复合丙烯酸乳液15-20％，玻璃珠25-28％，钛白粉15-20％，滑石粉12-15％，防沉剂1-2％，防冻剂0.5-1％，分散剂0.5-0.8％，润湿剂0.1-0.2％，消泡剂0.3-0.5％，pH调节剂0.2-0.3％，防腐剂0.2-0.6％，增稠剂0.2-0.5％，水20-25％。2.根据权利要求1所述的水性马路划线漆，其特征在于：所述钛白粉为金红石型钛白粉，二氧化钛含量大于95％，白度大于94％。3.根据权利要求1所述的水性马路划线漆，其特征在于：所述滑石粉为白色硅酸盐矿物，粒径为800-1250目，白度大于90％。4.根据权利要求1所述的水性马路划线漆，其特征在于：所述防沉剂为水性聚酰胺防沉剂，所述防冻剂为丙二醇。5.根据权利要求1所述的水性马路划线漆，其特征在于：所述分散剂为聚丙烯酸钠盐分散剂，固含40％。6.根据权利要求1所述的水性马路划线漆，其特征在于：所述润湿剂为脂肪醇烷氧基化物，所述消泡剂为有机硅类。7.根据权利要求1所述的水性马路划线漆，其特征在于：所述pH调节剂为2-氨基-2...
【专利技术属性】
技术研发人员：薛小倩，胡中源，董立志，刘洪亮，
申请(专利权)人：河北晨阳工贸集团有限公司，
类型：发明
国别省市：河北,13