The production process of anti-shattering glass for construction machinery windows is characterized by the following steps: (1) taking components according to the weight percentage and mixing them by ball milling to obtain mixed powder; (2) putting mixed powder into the smelting furnace and smelting at 1600 1800 for 4 6 hours to obtain glass liquid; (3) pouring glass liquid into storage container and then at 800 900 C. Heat treatment for 2 3 hours, cool to room temperature, take out the reserve. The glass produced by this process has superior fireproof property, can shield the flame, does not burst when burning at high temperature, and does not cause fragments to hurt people when broken. In addition, there are anti-theft performance, glass cutting and wire mesh blocking.
【技术实现步骤摘要】
一种工程机械车窗防碎玻璃的生产工艺
本专利技术涉及玻璃工艺品的制作工艺。具体涉及一种工程机械车窗防碎玻璃的生产工艺。
技术介绍
防碎安全玻璃是一类经剧烈振动或撞击不破碎,即使破碎也不易伤人的玻璃。包括钢化玻璃、夹层玻璃等。用于汽车、飞机和特种建筑物的门窗等。安全玻璃是由坚韧的塑料内层(PVB)将两片玻璃在一定温度和压力下粘贴而成,也称为夹层玻璃或胶合玻璃,其塑料内层可以吸收冲击和爆炸过程中所产生的部分能量和冲击波压力,即使被震碎也不会四散飞溅。夹层玻璃根据不同的需要可用普通玻璃、钢化玻璃、热增强玻璃来制成,也可制成中空玻璃。
技术实现思路
为了克服上述现有技术的不足,本专利技术提供一种工程机械车窗防碎玻璃的生产工艺,其成品光滑整洁无气孔,适合批量生产。一种工程机械车窗防碎玻璃的生产工艺,玻璃组分如下:玻璃组成含有以下组分SiO230-55份、CaO10-13份、K2O32-8份、Al2O39-12份。该生产工艺所述步骤如下:(1)按所述重量百分比取各组分,经球磨混合获得混合粉料;(2)将混合粉料投入到熔炼炉中,在1600-1800℃的温度下熔炼4-6小时,获得玻璃液;(3)将玻璃液倒入储存容器中,然后在800-900℃的温度下热处理2-3小时,冷却至室温,取出备用。进一步方案,所述的玻璃组分为:SiO235-40份、CaO11-13份、K2O36-8份、Al2O39-12份。进一步方案,所述步骤(2)中混合粉料在1750℃的温度下熔炼5-6h。进一步方案,所述步骤(3)中热处理时间为2.5h。本专利技术的有益效果是:防火性优越,可遮挡火焰,高温燃烧时不炸裂,破 ...
【技术保护点】
1.一种工程机械车窗防碎玻璃的生产工艺,其特征在于,包括如下步骤:玻璃组分如下:玻璃组成含有以下组分SiO230‑55份、CaO10‑13份、K2O32‑8份、Al2O39‑12份。
【技术特征摘要】
1.一种工程机械车窗防碎玻璃的生产工艺,其特征在于,包括如下步骤:玻璃组分如下:玻璃组成含有以下组分SiO230-55份、CaO10-13份、K2O32-8份、Al2O39-12份。2.一种工程机械车窗防碎玻璃的生产工艺,其特征在于,所述步骤如下:(1)按所述重量百分比取各组分,经球磨混合获得混合粉料;(2)将混合粉料投入到熔炼炉中,在1600-1800℃的温度下熔炼4-6小时,获得玻璃液;(3)将玻璃液倒入储存容器中,然后在800-900℃的温...
【专利技术属性】
技术研发人员:李秀芹,
申请(专利权)人:江苏智博工程机械科技有限公司,
类型:发明
国别省市:江苏,32