一种防火门芯板及其制备方法技术

本发明专利技术公开了一种防火门芯板，包括如下重量份的组分组成：氧化镁80～120份；硫酸镁40～50份；蛭石3～7份；石墨烯0.02～2份；KH5600.1～0.4份；CTAB0.1～0.4份；没食子酸基环氧树脂0.1～0.4份；聚丙烯短贴丝0.5～0.9份；发泡剂0.5～0.8份；稳泡剂0.0013～0.0065份；水100～120份。本发明专利技术还公开了所述防火门芯板的制备方法，所得防火门芯板密度为400‑484kg/m

A fireproof door core plate and its preparation method

The invention discloses a fire-proof door core board, which comprises the following components: 80-120 parts of magnesia; 40-50 parts of magnesium sulfate; 3-7 parts of vermiculite; 0.02-2 parts of graphene; KH5600.1-0.4 parts; CTAB0.1-0.4 parts; 0.1-0.4 parts of Gallic acid-based epoxy resin; 0.5-0.9 parts of polypropylene short filament; 0.5-0.8 parts of foaming agent; 0.0013-0.0065 parts of foaming stabilizer; 100-120 parts of water; \u3002 The invention also discloses the preparation method of the fire-proof door core plate, and the density of the fire-proof door core plate obtained is 400_484 kg/m.

【技术实现步骤摘要】
一种防火门芯板及其制备方法
本专利技术涉及建筑材料及制品
，更具体地说，它涉及一种防火门芯板及其制备方法。
技术介绍
目前，随着国家房地产行业的发展，防火建筑材料的需求越来越广，要求也越来越高。防火门具有封闭、阻火、隔断、安全、保温、隔音等多重功能和实用性，成为建筑防火系统中的重要组成部分，并越来越受到国家建筑部门及国家消防总局的高度重视。防火门施行许可证制度，生产防火门必须取得国家消防总局颁发的生产许可证，而防火门芯板是防火门必备的核心材料，在燃烧性能及安全性能上需要得到相关部门的形式检验，对防火门芯板的生产提出了更高的条件。目前来说，有如下两种防火门芯板，第一种是以硅酸铝棉为主要材料的门芯板，由于其烟气毒性指标达不到国家标准，现在已被明令禁止使用；另一种是以膨胀珍珠岩为主要材料的门芯板，由于珍珠岩的自身的强度差，与钢板或多层板粘结后，薄钢板的加工变形、遇热变形，以及碰撞变形等因素，容易导致防火门芯板碎裂，从而影响防火门的整体性能。多层板与珍珠岩制成的芯料板粘结后，在运输、安装过程中，受外力冲撞容易使芯料板破裂，在发生火灾时，当多层板燃尽后，防火门便自行散架失去防火作用。还有本文档来自技高网...

【技术保护点】
1.一种防火门芯板，其特征在于，包括如下重量份的组分组成：

【技术特征摘要】
1.一种防火门芯板，其特征在于，包括如下重量份的组分组成：2.根据权利要求1所述的一种防火门芯板，其特征在于，包括如下重量份的组分组成：3.根据权利要求2所述的一种防火门芯板，其特征在于，包括如下重量份的组分组成：4.根据权利要求1至3中任一项所述的一种防火门芯板，其特征在于，所述发泡剂为松香皂或十二烷基苯磺酸。5.根据权利要求1至3中任一项所述的一种防火门芯板，其特征在于，所述稳泡剂为十二烷基硫酸钠或α-烯基磺酸钠。6.一种制备权利要求1至3中任一项所述的防火门芯板的方法，其特征在于，包括如下步骤：1)将硫酸镁与蛭石溶于一定的水中，制成波美度为28°Bé-31°Bé的卤水；2)将石墨烯、KH560、CTAB加入到步骤1)所得的卤水中，搅拌均匀得清溶液；3)往步骤2)所得的清溶液中...

【专利技术属性】
技术研发人员：王晖，陈君齐，李翠翠，
申请(专利权)人：浙江星月安防科技有限公司，
类型：发明
国别省市：浙江,33