The invention discloses a fluorine modified asparagus polyurea paint and a preparation method thereof, which relates to the technical field of synthetic coatings. By creatively combining the advantages of asparagus polyurea and fluorocarbon coatings, the coating prepared by fluorine modified fluorine-containing polyaspartic acid ester resin can be applied to wind turbine blades, which can significantly improve the glass transition temperature, improve the high temperature resistance of the paint film, further improve the aging resistance, light loss resistance and color change resistance at high temperature, and reduce the water contact angle of the coating surface. It can reduce the wetting and erosion of water to paint film, improve the resistance to water, and improve the ability of anti-icing when wind turbine blades operate in low temperature and high humidity environment.
【技术实现步骤摘要】
一种氟改性天冬聚脲涂料及其制备方法
本专利技术涉及合成涂料
，尤其是指一种氟改性天冬聚脲涂料及其制备方法。
技术介绍
风电叶片涂料随着中国清洁能源的比重提高而规模不断扩大，因为风电叶片全天候，长时间在各种从夏季高温到冬季低温及风砂雨雪的各种天候工况下使用，同时风电叶片的长度达到60-80米，运转中的线速度高达60-80米每秒，在此高速下空气中的粉尘、风沙、雨滴、冰雪都会对风电叶片造成严重的磨蚀。风力发电机组的经济效益直接受稳定运行时间和停机维修频率的直接影响，因此对风电叶片涂料有极高的防护性能要求，例如对基材良好的附着力，耐雨蚀，-40℃低温伸长率，3000h老化，耐冷热湿循环，耐冷凝等。常规风电叶片涂料采用聚氨酯体系，存在耐老化性能不足，VOC排放高的缺点；聚天门冬氨酸酯聚脲体系的风电叶片涂料高固低VOC，环保性好，低温柔韧性优异，耐老化及耐雨蚀能满足要求，但是水接触角较低，与其他体系一样难以避免在低温高湿的雨雪天气造成覆冰。也有采用氟碳体系解决覆冰问题，同时耐候性优异，但是存在修复和重涂性能差，且刚性过强而低温柔韧性和耐雨蚀性能较低的问题。
技术实现思路
本...
【技术保护点】
1.一种氟改性天冬聚脲涂料，其特征在于，按重量份计，包括使用时再混合的A组分和B组分，组成为：A组分
【技术特征摘要】
1.一种氟改性天冬聚脲涂料，其特征在于，按重量份计，包括使用时再混合的A组分和B组分，组成为：A组分B组分固化剂20～200重量份；使用时A、B组分的混合重量比为5:1～1:2。2.如权利要求1所述的氟改性天冬聚脲涂料，其特征在于，按重量份计，包括使用时再混合的A组分和B组分，组成为：A组分B组分固化剂25重量份；使用时A、B组分的混合重量比为4:1。3.如权利要求1或2所述的氟改性天冬聚脲涂料，其特征在于，所述含氟聚天门冬氨酸酯树脂对应的结构式为：式中，R为脂肪烃基。4.如权利要求3所述的氟改性天冬聚脲涂料，其特征在于，按摩尔份计，所述含氟聚天门冬氨酸酯树脂合成的原料配方组成为：5.如权利要求1或2所述的氟改性天冬聚脲涂料，其特征在于，所述钛白粉选用金红石型钛白粉；所述分散剂选用高固含涂料用的大分子分散剂。6.如权利要求1或2所...
【专利技术属性】
技术研发人员：朱龙晖，邬茳，罗善锴，何飞云，王海波，鲁晓东，
申请(专利权)人：深圳飞扬骏研新材料股份有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。