The invention discloses a vacuum thermal creep forming method for titanium alloy skin, which comprises the following steps: 1) locating the clamp of the titanium alloy skin to be formed between the matching upper and lower dies; 2) heating the skin and the die under the vacuum environment, forming temperature is 700 900 C, and cooling with the furnace after holding a predetermined time; 3) removing the die and discharging the titanium combination. Gold skin forming is completed. Because of the creep forming of titanium alloy skin by integral vacuum heating and the gravity of the die itself, the tapping temperature is low, and the tapping temperature is below 150 C. After the tapping, the springback of the formed skin is small, the residual stress is small and the dimension precision is high.
【技术实现步骤摘要】
钛合金蒙皮的真空热蠕变式成形方法及钛合金蒙皮
本专利技术涉及航空制造
，特别是涉及一种钛合金蒙皮的真空热蠕变式成形方法及钛合金蒙皮。
技术介绍
钛合金蜂窝壁板结构具有质轻，比强度、比刚度高，隔热、消音降噪等优良特性，在航空航天领域有着广泛的应用，如AN-70飞机防火隔墙、F-15发动机罩、F-22发动机舱门等。对于钛合金蜂窝壁板结构一般采用钎焊方法进行连接，要保证其整体结构的焊合率，必须保证蒙皮与蜂窝芯体、蒙皮与蒙皮之间的贴合间隙小于0.1mm，且整个焊接面不得有氧化、凹坑等宏观缺陷。由于钛合金蜂窝壁板结构蒙皮较薄，一般1.0mm以下，采用传统热成形出炉温度高，蒙皮存在反弹、型面精度较低，也存在着高温氧化、吸氢等问题，导致母材性能下降，不能满足钛合金蜂窝壁板钎焊要求。因此，需开发一种适合的钛合金蒙皮成形方法。
技术实现思路
本专利技术的目的是针对现有技术中存在的技术缺陷，而提供一种钛合金蒙皮的真空热蠕变式成形方法及钛合金蒙皮。为实现本专利技术的目的所采用的技术方案是：一种钛合金蒙皮的真空热蠕变式成形方法，包括以下步骤，1）将待成形的钛合金蒙皮夹持定位在匹配的上模...
【技术保护点】
1.一种钛合金蒙皮的真空热蠕变式成形方法，其特征在于，包括以下步骤，1）将待成形的钛合金蒙皮夹持定位在匹配的上模具和下模具间；2）将蒙皮连同模具进行真空环境下加热，成形温度在700℃‑900℃，保温预定时间后随炉冷却后出炉；3）拆除模具，所述的钛合金蒙皮成形完成。
【技术特征摘要】
1.一种钛合金蒙皮的真空热蠕变式成形方法，其特征在于，包括以下步骤，1）将待成形的钛合金蒙皮夹持定位在匹配的上模具和下模具间；2）将蒙皮连同模具进行真空环境下加热，成形温度在700℃-900℃，保温预定时间后随炉冷却后出炉；3）拆除模具，所述的钛合金蒙皮成形完成。2.如权利要求1所述的钛合金蒙皮的真空热蠕变式成形方法，其特征在于，所述的步骤2）中真空度4×10-3~1×10-2Pa。3.如权利要求1所述的钛合金蒙皮的真空热蠕变式成形方法，其特征在于，所述的步骤2）保温1-5h。4.如权利要求1所述的钛合金蒙皮的真空热蠕变式成形方法，其特征在于，所述的步骤1）中还包括在上模具和下模具的表面设置阻焊剂的步骤。5.如权利要求4所述的钛合金蒙皮的真空热蠕变式成形方法，其特征在于，所述的阻焊剂颗粒度不...
【专利技术属性】
技术研发人员：岳喜山，高兴强，李辉，佀好学，潘鹏，
申请(专利权)人：中国航空制造技术研究院，
类型：发明
国别省市：北京,11