The invention relates to a low polarization aberration color plate and a preparation method thereof, belonging to the technical field of optical instruments. The present invention overcomes the shortcomings of large fluctuation of P and S light reflection phase and polarization aberration of the existing color splitter under the cone light incident condition; the present invention can not only realize the function of splitting light of the existing color splitter, but also effectively control the reflection phase of P and S light, and greatly reduce the influence of the use of the color splitter on the optical transfer function of the optical system; the use of the color splitter improves the imaging quality of the optical system.
【技术实现步骤摘要】
一种低偏振像差分色片及其制备方法
本专利技术涉及一种低偏振像差分色片及其制备方法,属于光学仪器
,可应用于光学分析仪器、光学探测器技术,低偏振像差是指在45°入射范围内,P光和S光的反射相位变化在一个周期内,反射相位数值不大于180°。
技术介绍
分色片是指在光线在一定角度入射下,部分光线被反射、部分光线透射,从而实现分色的目的,是众多光学系统的关键组成部分,广泛地应用于光学探测和光学测量中。其分光应用如图1所示,对于平行入射光,该系统能够实现部分入射光反射、部分光透射的功能。现有分色片在锥光入射条件下,由于光线在一定角度范围内入射,P光和S光的反射相移会不同,从而导致波阵面的相位存在差异,引入偏振像差。对于成像系统,其成像质量会下降,表现为子午和弧矢方向的传递函数变差。45°入射时,现有分色片的反射光谱和反射相位分别如图2、图3所示。由图3可以看出,当锥光入射时,经现有分色片反射后,P光、S光的反射相位出现大的波动,不同入射角度下的波阵面相位差异较大,从而引入偏振像差。对高质量成像光学系统,必须降低该类偏振像差。
技术实现思路
本专利技术解决的技术问题是:克服现有分色片的不足,提供了一种低偏振像差的分色片及其制备方法,解决了现有分色片在锥光入射时由于P偏振和S偏振光反射相移的大幅波动引入偏振像差的缺点。本专利技术的技术解决方案是:一种低偏振像差分色片,该分色片包括基底、二氧化钛层和二氧化硅层;所述的基底的材料为K9或石英等透明玻璃材料;二氧化钛层和二氧化硅层交替叠加;二氧化钛层的材料为二氧化钛薄膜,二氧化钛层在基底上;二氧化硅层的材料为二氧化硅薄膜;基 ...
【技术保护点】
1.一种低偏振像差分色片,其特征在于:该分色片包括基底、二氧化钛层和二氧化硅层。
【技术特征摘要】
1.一种低偏振像差分色片,其特征在于:该分色片包括基底、二氧化钛层和二氧化硅层。2.根据权利要求1所述的一种低偏振像差分色片,其特征在于:所述的基底为透明玻璃材料。3.根据权利要求1所述的一种低偏振像差分色片,其特征在于:所述的基底的材料为K9或石英。4.根据权利要求1所述的一种低偏振像差分色片,其特征在于:二氧化钛层和二氧化硅层交替叠加。5.根据权利要求1所述的一种低偏振像差分色片,其特征在于:二氧化钛层的材料为二氧化钛薄膜,二氧化钛层在基底上。6.根据权利要求1所述的一种低偏振像差分色片,其特征在于:二氧化硅层的材料为二氧化硅薄膜。7.根据权利要求1所述的一种低偏振像差分色片,其特征在于:二氧化钛层一共二十三层,二氧化硅层一共二十三层。8.根据权利要求1所述的一种低偏振像差分色片,...