The invention relates to the technical field of hot-coated steel plate, and discloses a semi-hot-coated steel plate, a production device and a production process. The semi-thermal coated steel plate comprises a metal substrate, one side of the surface of the metal substrate is coated with a fingerprint resistant layer, the other side of the surface of the metal substrate is coated with a coating layer, and the coating layer is bonded with a thermal coating film. The Semi-Hot clad steel plate production device and production process of the invention are used for automatically and continuously producing the Semi-Hot clad steel plate. The Semi-Hot clad steel plate of the invention saves composite film material, has good corrosion resistance and stamping resistance.
【技术实现步骤摘要】
一种半热覆膜钢板、生产装置及生产工艺
本专利技术涉及热覆膜钢板
，尤其是涉及一种半热覆膜钢板、生产装置及生产工艺。
技术介绍
热覆膜钢板广泛应用于电视背板、热水器等家电上，其以普通锌板作为基板，在锌板表面涂胶后，高温贴合PVC+PET复合膜，再经过冷却而成。现有的热覆膜钢板均为全热覆膜钢板，即在整个金属基板的表面均涂胶，并高温贴合PVC+PET复合膜，再经过冷却而成，由于复合膜的成本高，导致全热覆膜的生产成本较高，难以满足市场的需求。此外，由于有较多的后期加工，需要材料有良好的压延、拉伸性能。因全热覆膜钢板在金属钢板的表面全部覆有PVC+PET或PET膜，在较大的压延、拉伸加工下，会使热覆膜自身出现分层、破裂或从金属基板上脱离或剥离现象，因此其适用性受到较大影响。因此，设计一种半热覆膜钢板具有十分重要的意义。
技术实现思路
为了克服现有技术的不足，本专利技术提供一种半热覆膜钢板，在金属基板表面的一侧涂覆耐指纹层，另一侧上胶并热贴合复合膜，减小了复合膜的消耗，节省了成本，同时涂覆耐指纹层一侧具有良好的耐腐蚀性、抗冲压性，具有良好的后期处理性能。为了克服现有技术的不...
【技术保护点】
1.一种半热覆膜钢板，包括金属基板，其特征在于：所述金属基板表面的一侧涂覆有耐指纹层，所述金属基板表面的另一侧设有涂胶层，所述涂胶层上贴合有热覆膜。
【技术特征摘要】
1.一种半热覆膜钢板，包括金属基板，其特征在于：所述金属基板表面的一侧涂覆有耐指纹层，所述金属基板表面的另一侧设有涂胶层，所述涂胶层上贴合有热覆膜。2.根据权利要求1所述的半热覆膜钢板，其特征在于：所述金属基板包括冷轧板、热镀锌板、电镀锌板、镀铬板、铝板、镀铬板、电解板、不锈钢板、金属合金板中任一种；所述耐指纹层的厚度为0.8-1.2um；所述热覆膜包括PET-PVC膜、PET膜、金属膜中的任一种。3.根据权利要求1或2所述的半热覆膜钢板，其特征在于：所述耐指纹层通过在所述金属基板上涂覆耐指纹钝化液形成。4.一种半热覆膜钢板生产装置，用于生产如权利要求1-3中任一项所述的半热覆膜钢板，其特征在于：包括依次设置的脱脂清洗区、烘干区、涂覆辊组、第一烘烤区、上胶辊组、第二烘烤区、热覆机，所述涂覆辊组包括上下设置的涂覆辊与第一导料辊，所述涂覆辊与所述导料辊之间设有供物料通过的第一物料过道，所述涂覆辊的一侧设有涂覆区，所述上胶辊组包括上下设置的上胶辊与第二导料辊，所述上胶辊与所述第二导料辊之间设有第二物料过道，所述上胶辊相对于所述涂覆辊的另一侧设有上胶区。5.根据权利要求4所述的半热覆膜钢板生产装置，其特征在于：所述热覆机的后段设有冷却段。6.根据权利要...