The invention relates to a regeneration method of waste gypsum model, belonging to the field of gypsum, which comprises the following steps: (1) crushing: crushing waste gypsum model and sifting it through 60 to 80 meshes to obtain waste gypsum coarse particles; (2) primary purification: adding water to waste gypsum particles, mixing and filtering to obtain filter residue A; (3) secondary purification: adding filter residue A with hydrogen peroxide water, mixing and filtering to obtain filter residue B; (4) three times purification: Filtration residue B is added with water and adjusted to pH 4 108 This method can effectively remove impurities in waste gypsum model, and the gypsum powder obtained by this regeneration method has high strength for making gypsum model.
【技术实现步骤摘要】
一种废石膏模型的再生方法
本专利技术涉及石膏领域，具体涉及一种废石膏模型的再生方法。
技术介绍
卫生陶瓷产品是人们生活中的重要用品。生产卫生陶瓷的一个主要的成型方法是注浆成型，注浆成型大部分还是将泥浆在石膏模型中完成。石膏模型通常使用几十次就不能再用，成为报废的废石膏模型。日用瓷的生产也同样有大量报废的废石膏模型。据统计，每年国内仅仅用于制作陶瓷用品产生的废石膏模型就高达几百万吨。目前，废石膏模型的利用途径主要是水泥企业做部分原料使用，但使用量有限。所以不少陶瓷产区的废石膏模型都成为不好处理的垃圾。废石膏模型与天然石膏的主要成分都是二水硫酸钙，与天然石膏相比，废石膏模型的含水率比天然石膏高，此外，废石膏模型由于结构较为疏松，密度也较低。特别需要注意的是，废石膏模型中含有一定量的硫酸钠和无水硫酸钙使得再生的石膏粉强度较低，其中，硫酸钠易吸水膨胀，吸水膨胀产生的压力容易使制成的模型开裂导致再生石膏粉制作的石膏模型强度降低，并且硫酸钠还会缩短石膏粉的初终凝时间，卫生陶瓷用石膏模型的体积通常较大，倒模时间通常比较长，若初凝时间过短，则工人没有时间进行操作，导致难以完成灌浆...
【技术保护点】
1.一种废石膏模型的再生方法，其特征在于，包括以下步骤：(1)破碎：将废石膏模型破碎后过60‑80目筛得到废石膏颗粒；(2)一次纯化：在废石膏颗粒中加水，搅拌后过滤得滤渣A；(3)二次纯化：将滤渣A加双氧水，搅拌后过滤得到滤渣B；(4)三次纯化：将滤渣B加水并调节pH至4‑6，静置，除去上层清液，得下层沉淀物；(5)蒸压、烘干：将下层沉淀物进行蒸压，并干燥得到烘干料；(6)磨粉：将烘干料与聚丙烯酰胺混合后进行磨粉。
【技术特征摘要】
1.一种废石膏模型的再生方法，其特征在于，包括以下步骤：(1)破碎：将废石膏模型破碎后过60-80目筛得到废石膏颗粒；(2)一次纯化：在废石膏颗粒中加水，搅拌后过滤得滤渣A；(3)二次纯化：将滤渣A加双氧水，搅拌后过滤得到滤渣B；(4)三次纯化：将滤渣B加水并调节pH至4-6，静置，除去上层清液，得下层沉淀物；(5)蒸压、烘干：将下层沉淀物进行蒸压，并干燥得到烘干料；(6)磨粉：将烘干料与聚丙烯酰胺混合后进行磨粉。2.根据权利要求1所述的一种废石膏模型的再生方法，其特征在于，步骤(3)所述双氧水的浓度为5-10％，所述双氧水与所述滤渣A的质量之比为(3-5):1。3.根据权利要求1所述的一种废石膏模型的再生方法，其特征在于，步骤(2)所述废石膏颗粒和所述水的质量比为1:(3-5)。4.根据权利要求1所述的一种废石膏模型的再生方法，其特征在于，步骤(2)所述过滤...
【专利技术属性】
技术研发人员：李小满，
申请(专利权)人：厦门佳浴智能卫浴有限公司，
类型：发明
国别省市：福建,35