The invention relates to an ink material and its preparation method and application. The ink material comprises the following components: thermoplastic acrylic resin 30%-45%; acetic butyric acid fiber resin 5%-15%; polyketone resin 5%-10%; plasticizer 7%-15%; additive 2%-6%; filler 4%-9%; pigment 10%-25%; solvent 20%-30%. With thermoplastic acrylic resin as the main film-forming material, adding acetic acid butyric acid fiber resin and polyketone resin to improve the film-forming property of thermoplastic acrylic resin, the ink material has good printability, good adhesion, smooth film surface, and cooperates with plasticizers, auxiliaries, fillers, pigments and solvents to make the ink material drying fast, stable, strong adhesion and full color. It has strong covering power and is suitable for printing. It can be used for direct printing on the surface of plastic products. Ink materials meet the environmental protection testing standards of PAHS, REACH, SVHC, GB24613 2009, which are environmentally friendly and green.
【技术实现步骤摘要】
油墨材料及其制备方法与应用
本专利技术涉及油墨
，特别是涉及油墨材料及其制备方法与应用。
技术介绍
移印由于其工艺简单，速度快的优势，使其在塑胶产品上的印刷应用受到普遍的欢迎。但传统的用于移印的油墨材料仍具有以下不足：一、油墨材料的附着力较差，在移印后容易出现油墨脱落现象，导致生产良率不高，生产效率低的问题；二、油墨遮盖力不强，导致移印后的产品达不到理想的设计状态。
技术实现思路
基于此，本专利技术提供一种油墨材料，其具有附着力强、遮盖力强，且对环境友好，绿色环保。一种油墨材料，包括以下质量百分含量的组分：上述油墨材料，以热塑性丙烯酸树脂为主要成膜物质，加入醋酸丁酸纤维树脂和聚酮树脂改进热塑性丙烯酸树脂的成膜性，使油墨材料印刷性良好，黏连性佳，膜表面平整光滑，与增塑剂、助剂、填料、颜料及溶剂配合，使油墨材料干燥速度快，性质稳定，附着力强，且色彩饱满，遮盖力强，适用于移印，可应用于塑胶制品的表面直接移印；并且油墨材料符合PAHS、REACH、SVHC、GB24613-2009等环保检测标准，对环境友好，绿色环保。在其中一个实施例中，热塑性丙烯酸树脂的分子量为800...
【技术保护点】
1.一种油墨材料，其特征在于，包括以下质量百分含量的组分：
【技术特征摘要】
1.一种油墨材料，其特征在于，包括以下质量百分含量的组分：2.根据权利要求1所述的油墨材料，其特征在于，所述热塑性丙烯酸树脂的分子量为80000～100000。3.根据权利要求1所述的油墨材料，其特征在于，所述增塑剂为环已烷-1,2-二羧酸二异壬基酯。4.根据权利要求1所述的油墨材料，其特征在于，所述填料为疏水性二氧化硅。5.根据权利要求4所述的油墨材料，其特征在于，所述疏水性二氧化硅的粒径为7μm～9μm。6.根据权利要求1所述的油墨材料，其特征在于，所述溶剂选自异丙醇、异丁醇、环己酮中的一种或几种。7.根据权利要求1所述的油墨材料，其特征在于，所述助剂...