The invention belongs to the processing field of modified engineering plastics, and relates to a PC/PBT plastic alloy with strong impact resistance and fluidity and its preparation method. It is composed of the following materials in proportion: PC: 30-70 copies, PBT: 30-50 copies, compatible toughening agent: 3-7 copies, lubricant: 0.5-1 copies, antioxidant: 0.1-0.4 copies, demoulding agent: 0.2-0.5 copies. Among them, compatible toughening agent is one of KTR_6C, MBS, E/VAC, POE_g_MAH. The PC/PBT plastic alloy obtained by the formula and the manufacturing method of the invention improves the fluidity of the PC, improves the impact strength, and maintains the tensile strength and heat resistance. The raw material cost of PBT is much cheaper than that of PC. The PC/PBT alloy manufactured by the invention reduces the manufacturing cost and can be used in industrial production.
【技术实现步骤摘要】
一种抗冲击流动性强的PC/PBT塑料合金及其制备方法
本专利技术属于改性工程塑料领域，具体涉及一种抗冲击流动性强的PC/PBT塑料合金及其制备方法。
技术介绍
PC塑料具有高拉伸强度、高冲击强度、耐高温、优良的透明性，已广泛用在汽车、机械、电子电器、装修、日用品等领域；但它的流动性比较差，对注塑成型的加工产生了很大的影响，特别是在生产大件的产品时，易产生缺料和生产效率降低等问题，进而影响到冲击强度的下降，产品合格率降低。PBT是半结晶聚酯材料，由于其含有晶区，提高了抗化学品腐蚀的能力，且流动性好、易加工，但PBT本身刚性较大，缺口冲击强度较低、尺寸稳定性较差。由于在PC中加入部分的PBT，PBT分子插入PC分子之间，使PC分子之间的缠结力大大减小，PC分子的移动比较自由，从而提高了PC的流动性；PC与PBT共混物合金能够相互弥补二者的不足，且PC/PBT合金具有优良的加工流动性，良好的抗冲击性能，耐化学试剂的侵蚀，但由于原料的特性，其共混时存在相容性差的问题。丙烯酸酯与甲烯酸缩水甘油酯双官能化的乙烯类弹性体KTR-6C作为相容剂，可利用极性官能团之间的相互作用改善...
【技术保护点】
1.一种抗冲击流动性强的PC/PBT塑料合金，其特征在于，由以下组分按重量份配比而成：PC:30～70份，PBT:30～50份，相容增韧剂：3～7份，润滑剂：0.5～1份，抗氧剂：0.1～0.4份，脱模剂：0.2～0.5份。
【技术特征摘要】
1.一种抗冲击流动性强的PC/PBT塑料合金，其特征在于，由以下组分按重量份配比而成：PC:30～70份，PBT:30～50份，相容增韧剂：3～7份，润滑剂：0.5～1份，抗氧剂：0.1～0.4份，脱模剂：0.2～0.5份。2.根据权利要求1所述一种抗冲击流动性强的PC/PBT塑料合金，其特征在于，所述相容增韧剂为KTR-6C、MBS、E/VAC、POE-g-MAH的一种。3.一种抗冲击流动性强的PC/PBT塑料合金的制备方法，其特征在于，包括步骤：a.设置好挤出造粒机螺杆各段的温度加热值，加热升温；b.按配方比例称好各...
【专利技术属性】
技术研发人员：詹国春，
申请(专利权)人：厦门巧亿科技有限公司，
类型：发明
国别省市：福建,35
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。