The invention discloses a degradable polyester polylactic acid film and its preparation method. The bamboo raw fiber is modified by starch and carbon nanotubes, and then applied to the polyester polylactic acid film, which not only improves the electrostatic problem of the film, but also improves the toughness of the modified bamboo raw fiber, which can make the composite material form a three-dimensional network structure and strengthen it. The mechanical properties of the composites; carbon nanotubes not only exist in the composites as antistatic agents, but also act as bonding sites between the raw bamboo fibers and the base, promoting the bonding force between the raw bamboo fibers and the base, so as to improve the strength of the materials.
【技术实现步骤摘要】
一种可降解聚酯-聚乳酸薄膜及其制备方法
本专利技术属于降解材料
，具体涉及一种可降解聚酯-聚乳酸薄膜及其制备方法。
技术介绍
生物降解高分子材料具有无毒、可生物降解及良好的生物相容性等优点，所以其应用极为广泛，市场潜力非常大，包括医用、农业、工业包装、家庭娱乐等领域。在人工合成的可降解高分子中，聚乳酸和聚酯是最具代表性的聚合物，具有生物降解性能的材料，已广泛应用在我们的日常生活中。但是应用在雨衣领域时，因其容易产生静电而粘附在人身上，造成不平整，防雨效果不好等，令消费者苦恼不已。
技术实现思路
针对上述问题，本专利技术旨在提供一种具有抗静电性，力学性能良好的可降解聚酯-聚乳酸薄膜及其制备方法。本专利技术通过以下技术方案实现：一种可降解聚酯-聚乳酸薄膜，由以下重量份的原料制成：竹原纤维5-15，醋酸溶液100-200，聚乙二醇2-5，淀粉5-10，碳纳米管3-6，乙醇10-20，聚己内酯10-20，聚乳酸40-60，柠檬酸酯2-3，抗氧剂1-2；所述竹原纤维的长度为10-100μm，所述醋酸溶液浓度为3-5%。进一步的，其制备方法包括以下步骤：（1）将竹原纤维利用...
【技术保护点】
1.一种可降解聚酯‑聚乳酸薄膜，其特征在于，由以下重量份的原料制成：竹原纤维5‑15，醋酸溶液100‑200，聚乙二醇2‑5，淀粉5‑10，碳纳米管3‑6，乙醇10‑20，聚己内酯10‑20，聚乳酸40‑60，柠檬酸酯2‑3，抗氧剂1‑2；所述竹原纤维的长度为10‑100μm，所述醋酸溶液浓度为3‑5%。
【技术特征摘要】
1.一种可降解聚酯-聚乳酸薄膜，其特征在于，由以下重量份的原料制成：竹原纤维5-15，醋酸溶液100-200，聚乙二醇2-5，淀粉5-10，碳纳米管3-6，乙醇10-20，聚己内酯10-20，聚乳酸40-60，柠檬酸酯2-3，抗氧剂1-2；所述竹原纤维的长度为10-100μm，所述醋酸溶液浓度为3-5%。2.根据权利要求1所述的一种可降解聚酯-聚乳酸薄膜，其特征在于，其制备方法包括以下步骤：（1）将竹原纤维利用醋酸溶液的蒸气蒸腾30-40min，然后加入其体积100-150倍的蒸馏水中，加入聚乙二醇，升温至60-70℃，利用500-1000rpm的转速搅拌5-7h，然后冷却过滤，利用蒸馏水洗涤2-3次，然后放入30-40℃的鼓风干燥箱中干燥至含水率为5-8%；（2）将淀粉溶解与其体积10-20倍的蒸馏水中，在25-35℃，200-300rpm下搅拌20-40min，然后加入步骤（1）所得竹原纤维，提速至500-...
【专利技术属性】
技术研发人员：疏如，
申请(专利权)人：安徽宝玉雨具有限公司，
类型：发明
国别省市：安徽,34