The invention relates to a modified nano barium sulfate reinforced polypropylene film and a preparation method thereof, belonging to the technical field of functional packaging materials. The modified nano-barium sulfate was used as toughening agent, organic montmorillonite and maleic anhydride grafted polyethylene as compatibilizing agent, adding certain reinforcing agent, PP as base material, and the film was prepared by blow-moulding. The invention prepared a reinforced polypropylene composite film with good heat resistance, high barrier property, certain flame retardant property, high tensile property, breaking elongation and good aging resistance, which can be widely used in daily necessities, household appliances and other fields.
【技术实现步骤摘要】
一种改性纳米硫酸钡增强聚丙烯膜及其制备方法
本专利技术涉及一种改性纳米硫酸钡增强聚丙烯膜及其制备方法，属于功能包装材料
技术介绍
随着工业的不断发展，高分子材料广泛应用，各个领域对材料性能的要求不断提升。为了满足应用的需要，单纯纯树脂制成的材料显得力不从心，所以，高分子材料领域必须推陈出新，塑料改性的研究也就越来越重要，例如期望聚合物材料耐高温、易于加工成型、具有很好的韧性、较高的强度、性能良好而且价格低廉等等。单一的均聚物材料往往难以满足上述要求，因此可以通过纳米复合技术对现有聚合物材料进行改性，可以制成综合性能优异的新型高分子材料，已成为新材料开发领域的重要研究方向，具有广阔的市场开发应用前景。聚丙烯(PP)是一种工业产量较大的聚合物，它具有质轻、易于加工、化学稳定性良好等优点，在电子产品、汽车零件、包装材料等领域的应用十分广泛，但PP的耐候性和低温韧性不高，使其在某些方面的应用受到了限制。而通过纳米改性不仅能够弥补这些方面的不足，选择特定的功能材料还能提升PP的力学性能。纳米粒子尺寸和彼此间距离特别近，具有独特的量子尺寸效应、表面效应、界面效应等等...
【技术保护点】
1.一种改性纳米硫酸钡增强聚丙烯膜，其特征是按重量百分比计组分为：纳米硫酸钡10‑30份、马来酸酐接枝聚乙烯3‑10份、聚丙烯树脂60‑80份、有机蒙脱土3‑8份、偶联剂0.1‑5份、增强剂7‑10份；首先采用偶联剂对纳米硫酸钡进行改性，得到改性纳米硫酸钡；然后以改性纳米硫酸钡为增韧剂、有机蒙脱土和马来酸酐接枝聚乙烯为增容剂，加入增强剂，以聚丙烯树脂为基材，经吹塑成膜制得。
【技术特征摘要】
1.一种改性纳米硫酸钡增强聚丙烯膜，其特征是按重量百分比计组分为：纳米硫酸钡10-30份、马来酸酐接枝聚乙烯3-10份、聚丙烯树脂60-80份、有机蒙脱土3-8份、偶联剂0.1-5份、增强剂7-10份；首先采用偶联剂对纳米硫酸钡进行改性，得到改性纳米硫酸钡；然后以改性纳米硫酸钡为增韧剂、有机蒙脱土和马来酸酐接枝聚乙烯为增容剂，加入增强剂，以聚丙烯树脂为基材，经吹塑成膜制得。2.如权利要求1所述改性纳米硫酸钡增强聚丙烯膜，其特征是：所述纳米硫酸钡体征维度尺寸为1-100nm。3.如权利要求1所述改性纳米硫酸钡增强聚丙烯膜，其特征是：所述偶联剂为酞酸酯偶联剂和/或铝酸酯偶联剂。4.如权利要求1所述改性纳米硫酸钡增强聚丙烯膜，其特征是：所述增强剂为纳米高岭土和/或微晶白云母。5.如权利要求1所述改性纳米硫酸钡增强聚丙烯膜，其特征是：所述增容剂为有机蒙脱土、马来酸酐接枝聚乙烯、马来酸酐接枝聚丙烯中的一种或几种的混合物。6.权利要求1所述改性纳米硫酸钡增强聚丙烯膜，其特征是按重量份计步骤为：(1)改性纳米硫酸钡制取：a、取纳米硫酸钡10-30份，加入250-280份无水乙醇，再加入0...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。