一种凹凸棒石改性复合肥制造技术

本发明专利技术涉及一种凹凸棒石改性复合肥，其特征在于由下列各组分按重量百分比混合制备；凹凸棒石粉10‑20%，尿素10‑20%，硫酸铵15‑20%，硫酸钾20‑30%，磷酸一铵25‑35%，碳酸氢铵3‑5%，硫酸脲溶液5‑8%。合理利用了硫酸与水、尿素与硫酸的反应热，造粒机内蒸汽用量也因硫酸脲溶液具有高黏性而大幅降低，节能效果明显。可实现连续生产，提高了生产效率。

A Compound Fertilizer Modified by Attapulgite

The invention relates to a modified attapulgite compound fertilizer, which is characterized by mixing the following components according to weight percentage; attapulgite powder 10 20%, urea 10 20%, ammonium sulfate 15 20%, potassium sulfate 20 30%, monoammonium phosphate 25 35%, ammonium bicarbonate 3 5%, urea sulfate solution 5 8%. Reaction heat between sulfuric acid and water, urea and sulfuric acid was rationally utilized. The steam consumption in granulator was also greatly reduced due to the high viscosity of urea sulfate solution, and the energy saving effect was obvious. It can realize continuous production and improve production efficiency.

【技术实现步骤摘要】
一种凹凸棒石改性复合肥
本专利技术涉及肥料生产
，特别是一种凹凸棒石改性复合肥。
技术介绍
复合肥外观一般为颗粒状，主要原料有硫酸铵、硝酸铵、尿素、硫酸钾、氯化钾等。具有养分含量高、副成份少且物理性状好等优点，对于平衡施肥，提高肥料利用率，促进作物高产稳产具有十分重要的作用。凹凸棒矿改性复合肥具有纳米多孔道柱状结构，特有的吸附性能可吸附氮素的损耗；也有利于保存磷钾等养分，提高了肥料的利用率，减少了有效养分的流失。现有技术生产凹凸棒性复合肥，一般是先酸化凹凸棒石粉，将凹凸棒石粉与硫酸混合后进行堆放。这种方式堆放场地大，还需不停的翻搅，混合不均匀，无法实现连续化生产。
技术实现思路
本专利技术的目的在于避免现有技术的不足，提供一种凹凸棒石改性复合肥。为实现上述目的，本专利技术采取的技术方案为：一种凹凸棒石改性复合肥，其特征在于由下列各组分按重量百分比混合制备；凹凸棒石粉10%-20%，尿素10-20%，硫酸铵15-20%，硫酸钾20-30%，磷酸一铵25-35%，碳酸氢铵3-5%，硫酸脲溶液5-8%；其制备方法包括如下步骤：a.制备凹凸棒石细粉：将凹凸棒石黏土矿物经手选→干燥→破碎→磨本文档来自技高网...

【技术保护点】
1.一种凹凸棒石改性复合肥，其特征在于由下列各组分按重量百分比混合制备；凹凸棒石粉 10‑20%，尿素 10‑20%，硫酸铵 15‑20%，硫酸钾 20‑30%，磷酸一铵 25‑35%，碳酸氢铵 3‑5%，硫酸脲溶液 5‑8%；其制备方法包括如下步骤：a.制备凹凸棒石细粉：将凹凸棒石黏土矿物经手选→干燥→破碎→磨矿→分级，制成100目‑150目的细粉，含水量≤15%，颜色为灰白色或红色；b.制备硫酸脲溶液：将93%的硫酸、尿素、水按质量比1:2：0.1的混合搅拌均匀，温度控制40‑60℃；c.造粒：将凹凸棒石粉、尿素 、硫酸铵 、硫酸钾，磷酸一铵，碳酸氢铵按比例加入造粒机，再将硫酸脲溶液雾化喷...

【技术特征摘要】
1.一种凹凸棒石改性复合肥，其特征在于由下列各组分按重量百分比混合制备；凹凸棒石粉10-20%，尿素10-20%，硫酸铵15-20%，硫酸钾20-30%，磷酸一铵25-35%，碳酸氢铵3-5%，硫酸脲溶液5-8%；其制备方法包括如下步骤：a.制备凹凸棒石细粉：将凹凸棒石黏土矿物经手选→干燥→破碎→磨矿→分级，制成100目-150目的细粉，含水量...

【专利技术属性】
技术研发人员：魏玉祥，王晨晖，
申请(专利权)人：白银丰宝农化科技有限公司，
类型：发明
国别省市：甘肃,62