The invention relates to the field of ceramic forming technology, in particular to a cerium dioxide microsphere, its preparation method and use. The method comprises the following steps: mixing citric acid cerium, six methylene four amine, urea, N, N methylene bis acrylamide, acrylic acid and ammonium persulfate to obtain precursor solution; dispersing the precursor solution into silicone oil so as to obtain gel balls; and baking the treated gel balls so as to obtain two cerium oxide microspheres. The cerium dioxide ceramic microspheres prepared by the method of the invention have high strength, no defect or breakage occurs in the washing process, and the process is simple, and the damage to the environment is small.
【技术实现步骤摘要】
共聚合辅助内凝胶法制备CeO2陶瓷微球的方法
本专利技术属于陶瓷成型工艺领域，具体涉及一种二氧化铈陶瓷微球及其制备方法和用途，尤其涉及一种通过共聚合辅助内凝胶法制备二氧化铈微球的方法，以及通过该方法制备得到的二氧化铈微球和用途。
技术介绍
随着我国核能技术的发展，乏燃料的累积量将会逐渐增多，其中包含可循环使用的235U、238U、Pu、中短寿命的裂变产物、次锕系元素和长寿命裂变产物。对乏燃料的潜在危害性分析表明，其远期风险主要来自于Np、Am、Cm等次锕系元素和长寿命裂变产物，需要经过几万甚至几十万年其放射水平才能降到天然铀矿的水平，这就需要一种高效处理次锕系元素和长寿命裂变产物的方法。自二十世纪九十年代初以来，一些先进核能国家已经对加速器驱动的次临界系统(AcceleratorDrivenSub-criticalSystem,ADS)开展了深入的研究，其安全性和嬗变核废料的能力已经获得广泛的国际认可。研究表明，在含有U的次临界系统的反应堆堆芯中，U通过中子俘获反应以及衰变过程会转换成次锕系元素等，进而影响系统的嬗变效率。因此，为了提高系统的嬗变效率，无铀的核燃料...
【技术保护点】
1.一种制备二氧化铈微球的方法，其特征在于，包括：将柠檬酸铈、六次甲基四胺、尿素、N,N‑亚甲基双丙烯酰胺、丙烯酸和过硫酸铵混合，以便得到前驱体溶液；将所述前驱体溶液分散到硅油当中，以便得到凝胶球；将所述凝胶球进行焙烧处理，以便得到二氧化铈微球。
【技术特征摘要】
1.一种制备二氧化铈微球的方法，其特征在于，包括：将柠檬酸铈、六次甲基四胺、尿素、N,N-亚甲基双丙烯酰胺、丙烯酸和过硫酸铵混合，以便得到前驱体溶液；将所述前驱体溶液分散到硅油当中，以便得到凝胶球；将所述凝胶球进行焙烧处理，以便得到二氧化铈微球。2.根据权利要求1所述的方法，其特征在于，所述六次甲基四胺、尿素的含量比为：2.0～2.6(mol)：2.0～2.6(mol)。任选地，所述丙烯酸的加入量为0.5～2mL，所述过硫酸铵的加入量为0.04～0.2g；任选地，所述N,N-亚甲基双丙烯酰胺的加入量为0.02～0.1g。3.根据权利要求1或2所述的方法，其特征在于，所述硅油的温度在85摄氏度以上，优选为85～90摄氏度。4.根据权利要求1～3中任一项所述的方法，其特征在于，所述焙烧处理是先在Ar气气氛下于600摄氏度焙烧，再在空气气氛下于600摄氏度以上。5.根据权利要求1～4中任一项所述的方法，其特征在于，所述柠檬酸铈通过将铈盐和柠檬酸混合制备得到；任选地，所述铈盐和所述柠檬酸的摩尔量比为(1.6～2)：(1.4～2)；任选地，所述铈盐选自下列至少之一：硝酸铈、氯化铈、硫酸铈或醋酸铈。6.根据权利要...
【专利技术属性】
技术研发人员：丁学强，马景陶，赵兴宇，郝少昌，邓长生，刘兵，
申请(专利权)人：清华大学，
类型：发明
国别省市：北京,11