The invention discloses an alumina ceramic ball and a preparation method thereof. Among them, alumina ceramic balls are mainly made of the following raw materials by weight percentage: high temperature ceramic roller scrap 40 60%, alumina powder 30 50%, zirconium powder 2 10%, barium carbonate 2 6%, dolomite 0.1 2% and bentonite 1 4%. The invention adopts ceramic roller scrap as main raw material, adds a certain amount of alumina powder and zirconium powder, and uses barium carbonate as main flux, so that the alumina ceramic ball not only has the common characteristics of high specific gravity, high strength (hardness), high wear resistance and other ordinary alumina ceramic balls, but also has the high toughness that ordinary alumina ceramic balls are difficult to achieve, and is suitable for dry grinding and high impact. Force and high temperature environment not only recycle waste, but also reduce the cost of ceramic balls.
【技术实现步骤摘要】
一种氧化铝陶瓷球及其制备方法
本专利技术涉及陶瓷球
，尤其涉及一种氧化铝陶瓷球及其制备方法。
技术介绍
氧化铝陶瓷球广泛应用于陶瓷、玻璃、搪瓷、颜料、化工等行业，是各类磨机细碎设备中的研磨球体，其强度高，密度大，磨耗小，耐腐蚀，适用性强，粉碎效率高。现有的高端氧化铝陶瓷球主要用于磨制陶瓷釉料，水泥干磨等需要高效及清洁的耐磨材料。其中，水泥行业的粉料细磨普遍使用耐磨钢球，其中含有氧化铬类等重金属，会对环境产生不利的影响，随道环保要求的提高，以及技术的进步，近年来，氧化铝耐磨球在水泥行业的干磨得到了推广。但用于水泥干磨的氧化铝陶瓷球的强度要求高，需要较高的强度和韧性，以克服在使用过程中易产生的碎裂现象。目前氧化铝陶瓷球的制备方法包括两种：一、以氧化铝粉作为主要原料，并对其进行煅烧。通过煅烧氧化铝粉生产的氧化铝陶瓷球外观白色，产品质量较好，耐磨性好，但对资源消耗大，生产成本高。其中，在进行干磨的场合，产品的强度要求高，普通氧化铝陶瓷球易产生碎裂的现象。二、以铝矾土作为主要原料，并对其进行煅烧。通过煅烧铝矾土生产的氧化铝陶瓷球外观黄色，产品质量相对稍差，且适应性较差...
【技术保护点】
1.一种氧化铝陶瓷球，其特征在于，其主要由以下以重量百分比计的原料制成：
【技术特征摘要】
1.一种氧化铝陶瓷球，其特征在于，其主要由以下以重量百分比计的原料制成：其中，所述高温陶瓷辊棒废料包括以下组分：2.如权利要求1所述的氧化铝陶瓷球，其特征在于，其主要由以下以重量百分比计的原料制成：3.如权利要求1所述的氧化铝陶瓷球，其特征在于，所述高温陶瓷辊棒废料包括以下组分：4.如权利要求3所述的氧化铝陶瓷球，其特征在于，所述高温陶瓷辊棒废料包括以下组分：5.如权利要求1所述的氧化铝陶瓷球，其特征在于，所述废锆粉包括以下组分：6.如权利要求5所述的氧化铝陶瓷球，其特征在于，所述废锆粉包括以下组分：7.如权利要求1所述的氧化铝陶瓷球，其特征在于，所述氧化铝陶瓷球包括以下组分：8.一种如权利要求1-7任一项所述的氧化铝陶瓷球的制备方法，...
【专利技术属性】
技术研发人员：冯斌，张脉官，唐涛，李纲举，
申请(专利权)人：萍乡市金刚科技工业园有限公司，
类型：发明
国别省市：江西,36