一种三氧化二铁颜料一步氧化方法技术

本发明专利技术公开了一种三氧化二铁颜料一步氧化方法，通过往氧化桶中先加入三氧化二铁晶种，鼓空气2‑3h，然后加入硝酸亚铁，直接升温、加空气氧化，一步反应制得。本发明专利技术整个氧化过程中不加水，在加入与二步氧化同等量的硝酸亚铁的情况下，保证了硝酸亚铁的浓度，使反应体系中的硝酸亚铁含量由3%增加到6%以上，从而提高了产品质量，产品的着色力效果得以提升，颜色色泽好，产品色相更加饱和、鲜艳。

One-step oxidation of iron oxide pigments

The invention discloses a one-step oxidation method for ferrous oxide pigments, which is prepared by adding ferrous oxide crystal seeds into the oxidation barrel, blowing air for 2 3 h, then adding ferrous nitrate, heating directly, air oxidation and one-step reaction. The invention does not add water in the whole oxidation process, and ensures the concentration of ferrous nitrate when adding the same amount of ferrous nitrate as the second step oxidation, so that the content of ferrous nitrate in the reaction system increases from 3% to more than 6%, thereby improving the product quality, improving the coloring effect of the product, having good color and luster, and making the product more saturated and bright.

【技术实现步骤摘要】
一种三氧化二铁颜料一步氧化方法
本专利技术涉及一种三氧化二铁颜料一步氧化方法，属于氧化铁红颜料生产

技术介绍
氧化铁红具有良好的颜色遮盖力、着色力、耐热、耐溶剂、耐酸性、无毒、防锈等性能，是优质的颜料品种，可广泛用于涂料、油墨、塑料、橡胶、纺织、陶瓷、美术水泥、化妆品等。目前，三氧化二铁的生产工艺一般可分为煅烧法、直接氧化法、水热法以及沉淀法，其中直接氧化法具体指的是氧化铁红的二步氧化法，即第一步氧化，即往氧化桶内加入原料铁皮、水、晶种、硝酸亚铁反应；第二步氧化，即继续往二步氧化桶中加入硫酸亚铁和水。在上述这种二步氧化反应中，加水两次，稀释了硝酸亚铁的浓度，影响最终的着色效果，即影响颜料的色泽。
技术实现思路
针对上述现有技术存在的不足，本专利技术的目的是提供一种工艺设计更为合理的三氧化二铁颜料一步氧化方法。为实现上述目的，本专利技术采用的技术方案：三氧化二铁颜料一步氧化方法，其特征在于，往氧化桶中先加入铁皮、三氧化二铁晶种，鼓空气2-3h，然后加入硝酸亚铁，直接升温、加空气氧化，一步反应制得。优选地，上述空气的流速为5-30m³/min。优选地，上述硝酸亚铁与三氧化二铁晶种的本文档来自技高网...

【技术保护点】
1.一种三氧化二铁颜料一步氧化方法，其特征在于，往氧化桶中先加入三氧化二铁晶种、铁皮，鼓空气2‑3h，然后加入硝酸亚铁，直接升温、加空气氧化，一步反应制得。

【技术特征摘要】
1.一种三氧化二铁颜料一步氧化方法，其特征在于，往氧化桶中先加入三氧化二铁晶种、铁皮，鼓空气2-3h，然后加入硝酸亚铁，直接升温、加空气氧化，一步反应制得。2.根据权利要求1所述的三氧化二铁颜料一步氧化方法，其特征在于，上述空气的流速为5-30m...

【专利技术属性】
技术研发人员：张清敏，肖剑，张柏梁，赵俊海，陈启波，
申请(专利权)人：湖南冠一颜料有限公司，
类型：发明
国别省市：湖南,43