The invention discloses a composite injection desulfurizer for hot metal and its desulfurization process. The desulfurizer includes passivation magnesium, lime and limestone. The passivation magnesium includes lime: limestone mass ratio is 1:2-8:1-4; the diameter of passivation magnesium particle is 0.6-0.1 mm; the size of lime is 200-300 meshes; the size of limestone is 300-400 meshes; the desulfurization process is to inject passivation magnesium, lime and limestone into hot metal. Limestone is used as desulfurizer for hot metal desulfurization; passivation magnesium: lime: limestone mass ratio is 1:2-8:1-4; the relationship between passivation magnesium particle diameter and spray gun insertion depth is as follows: d = Y [6.75*10].
【技术实现步骤摘要】
复合喷吹铁水脱硫剂及其脱硫工艺
本专利技术涉及冶金
，具体地指一种复合喷吹铁水脱硫剂及其脱硫工艺。
技术介绍
目前，铁水脱硫主要有：KR(机械搅拌)脱硫、单吹颗粒镁脱硫和复合喷吹脱硫。复合喷吹铁水脱硫工艺是近些年来国内外发展起来的铁水脱硫工艺，由于其灵活性、自动化程度高所以被广泛应用于铁水脱硫。传统的复合喷吹脱硫工艺多为钝化镁－石灰复合喷吹脱硫，其实质就是用钝化镁、石灰按一定比例从喷枪中复合喷吹进入铁水，与铁水中的硫反应，生成硫化物上浮以脱硫。现有的复合喷吹脱硫主要存在以下问题：1)由于镁进入铁液后，形成的镁气泡直径大，上浮速度快，所以利用率低，导致镁的消耗高；2)喷吹脱硫与搅拌脱硫相比，搅拌动力学条件不足，脱硫剂与铁水反应不够充分，导致脱硫率低；3)脱硫效果不稳定，容易出现脱硫效果差的问题。
技术实现思路
本专利技术的目的就是要提供一种复合喷吹铁水脱硫剂及其脱硫工艺，该脱硫剂脱及其脱硫工艺硫效果好，脱硫成本低。为实现上述目的，本专利技术采用的技术方案是：一种复合喷吹铁水脱硫剂，所述脱硫剂包括钝化镁，石灰和石灰石，所述钝化镁：石灰：石灰石的质量比为1：2～8：1...
【技术保护点】
1.一种复合喷吹铁水脱硫剂，其特征在于：所述脱硫剂包括钝化镁，石灰和石灰石，所述钝化镁：石灰：石灰石的质量比为1：2～8：1～4；钝化镁颗粒直径为0.6～0.1mm；石灰粒度为200～300目；石灰石粒度为300～400目。
【技术特征摘要】
1.一种复合喷吹铁水脱硫剂，其特征在于：所述脱硫剂包括钝化镁，石灰和石灰石，所述钝化镁：石灰：石灰石的质量比为1：2～8：1～4；钝化镁颗粒直径为0.6～0.1mm；石灰粒度为200～300目；石灰石粒度为300～400目。2.根据权利要求1所述复合喷吹铁水脱硫剂，其特征在于：钝化镁：石灰：石灰石的质量比为1：5：2。3.一种复合喷吹铁水脱硫工艺，其特征在于：向铁水中吹入钝化镁，石灰和石灰石作为脱硫剂进行铁水脱硫；钝化镁：石灰：石灰石的质量比为1：2～8：1～4；钝化镁颗粒直径与喷枪插入深度满足如下关系式：d＝Y[6.75×10－6h(1+0.625h)1/2]2/3，Y为前置系数，取值0.8～1.2；h为喷枪插入深度，单位为m；d为钝化镁颗粒直径，单位为mm。4.根据权利要求3...
【专利技术属性】
技术研发人员：孙伟，朱万军，齐江华，陈俊孚，杨成威，张剑君，
申请(专利权)人：武汉钢铁有限公司，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。