The invention discloses a UV curable waterproof adhesive, a preparation method and application thereof. The UV curable waterproof adhesives of the invention are prepared from 20-35 parts of modified levodopa, 65-80 parts of acrylate monomer, 0.1-1 part of initiator and 100-150 parts of solvent. The UV curable waterproof adhesive has the advantages of simple preparation process, small amount of adhesives and excellent waterproof bonding performance, no degumming during peeling process, and is suitable for waterproof sealing protection of overhead insulated conductor joints, waterproof sealing of machine heads of various types of wires and cables and communication cables.
【技术实现步骤摘要】
一种UV固化防水胶粘剂、其制备方法及应用
本专利技术涉及胶粘剂
，具体涉及一种UV固化防水胶粘剂、其制备方法及应用。
技术介绍
胶粘剂是一种具有很好粘合性能的物质。通过粘附力和内聚力由表面粘合而起连接物体的作用。由于其自身特点导致粘接剂在市场上具有非常广泛的应用，应用领域包括生活用品、电子产品包装用的屏蔽保护膜、电器电工用的绝缘胶带等。丙烯酸酯类压敏胶是目前应用最为广泛的胶粘剂之一，它是丙烯酸酯单体和其它乙烯类单体的共聚物，其具有以下特点：1)几乎不用加防老剂便具有优异的耐候性和耐热性；2)无相分离和迁移现象，透明性好，耐油性差；3)对皮肤无影响，适用于医用领域，丙烯酸酯类的压敏胶用量占到整个压敏胶用量的65％以上，尤其是近二十年来这类压敏胶发展非常迅速，并逐渐取代了天然橡胶压敏胶的地位。自然界中的动植物经过40多亿年的进化使其能够适应严格的自然环境，其中结构与功能达到了完美的程度。其中，贻贝是最经典的一个例子，贻贝是一种软体动物，隶属于贻贝科，其生长环境主要是海洋及沿海周边地区，而且特别喜欢生活在冷水海域中，这些环境都十分潮湿和严苛，但贻贝分泌的足丝能够在...
【技术保护点】
1.一种UV固化防水胶粘剂，其特征在于，由下述重量份的原料制备而成：
【技术特征摘要】
1.一种UV固化防水胶粘剂，其特征在于，由下述重量份的原料制备而成：2.根据权利要求1所述的UV固化防水胶粘剂，其特征在于，所述改性左旋多巴由下述重量份的原料制备而成：称取50g左旋多巴、80g四硼酸钠、30g碳酸氢钠和1500mL去离子水并倒入装有氮气管、搅拌器的烧瓶中并加热溶解，控制温度50～55℃，将500mL、8wt％的丙烯酰氯四氢呋喃溶液慢慢滴加进烧瓶中，调节pH>7，然后在30℃条件下通氮气反应12h，过滤出固体残渣后，加2000mL乙酸乙酯，调节剩余溶液的pH<2，最后进行萃取，将水层去除掉，剩余有机层滴加到正己烷中沉淀出最终产物，将最终产物过滤进行真空干燥。3.根据权利要求1所述的UV固化防水胶粘剂，其特征在于，所述丙烯酸酯单体包括丙烯酸丁酯、丙烯酸异辛酯、丙烯酸异丁酯、丙烯酸仲丁酯、丙烯酸正丙酯、丙烯酸-2-羟基丙酯、甲基丙烯酸月桂酯、丙烯酸乙酯、丙烯酸甲酯、甲基丙烯酸乙酯、甲基丙烯酸甲酯、甲基丙烯酸正丁酯、丙烯酸叔丁酯、甲基丙烯酸-2-羟丙酯、丙烯酸、甲基丙烯酸、丙烯酸羟乙酯、丙烯酰胺、马来酸酐、甲基丙烯酸缩水甘油酯中、乙酸乙烯酯和苯乙烯中的一种或多种。4.根据权利要求1所述的UV固化防水胶粘剂，其特征在于，所述引发剂包括偶氮二异丁腈和过氧化二苯甲酰中的一种或两种。5.根据权利要求1所述的UV固化防水胶粘剂，...
【专利技术属性】
技术研发人员：贺金梅，张晓勇，白永平，岳利培，
申请(专利权)人：哈尔滨工业大学无锡新材料研究院，无锡海特新材料研究院有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。