The invention discloses a polycarboxylic acid superplasticizer, which belongs to the field of chemical industry. The raw materials used in the production of this product include: acrylic acid 8%-9%, sodium methacrylate 2%-3%, maleic anhydride 4%, sodium persulfate 2%, calcium hydroxide 3%, deionized water 80% by mixing method to produce polycarboxylic acid superplasticizer. The product is non-toxic and suitable for various kinds of cement. The advantages are as follows: 1. It can protect the separation of raw materials, thus making concrete of the same quality; 2. It has good usability for a long time; 3. Reducing flooding to reduce the depth of concrete; 4. It has good water reducing effect and slump retention, high water reducing rate, good concrete and ease of use.
【技术实现步骤摘要】
一种聚羧酸高效减水剂
本专利技术产品属化工领域，尤其涉及一种聚羧酸高效减水剂的生产方法。
技术介绍
聚羧酸高效减水剂外观为浅棕色液体，固含量22%，减水率25%-45%，泌水率比≤20%，常用掺量为0.8-1.5%，聚羧酸高效减水剂与水泥的适应性好，其优点是：1.掺量低、减水率高，减水率最高可达45%；2.坍落度轻时损失小；3.混凝土工作性好，外观颜色均一；4.混凝土收缩小，产品稳定性好；5.碱含量极低；6.产品无毒无害，是绿色环保产品。生产本产品使用的原料有：丙烯酸、甲基丙烯酸钠、马来酸酐、过硫酸钠、氢氧化钙、去离子水，并辅以一定的工艺条件来生产减水剂，产品的优点是：1.无毒，适用于各种水泥；2.可保护原料的分离，从而制造品质一致的混凝土；3.较长时间内拥有良好的可使用性；4.减少泛浆而减少混凝土的深淀；5.具有良好的减水效果和保坍性，减水率高、混凝土和易性好。
技术实现思路
本专利技术要解决的问题是提供一种批量生产聚羧酸高效减水剂的方法，生产该产品使用的原料按重量配比包括：丙烯酸8%-9%、甲基丙烯酸钠2%-3%、马来酸酐4%、过硫酸钠2%、氢氧化钙3%、去离子水...
【技术保护点】
1.一种聚羧酸高效减水剂，生产该产品使用的原料按重量配比包括：丙烯酸8%‑9%、甲基丙烯酸钠2%‑3%、马来酸酐4%、过硫酸钠2%、氢氧化钙3%、去离子水80%，其特征是：（1）用5个搅拌容器分别将配方量的丙烯酸、甲基丙烯酸钠、马来酸酐、过硫酸钠、氢氧化钙配制成浓度20%的水溶液；（2）将丙烯酸、甲基丙烯酸钠、马来酸酐、过硫酸钠、氢氧化钙的20%水溶液同时送入化学反应釜，开始搅拌，边搅拌边将缓慢的将温度提高至42‑44℃，搅拌反应1.0‑1.2小时；继续搅拌，降温至常温停止搅拌出料，得到成品。
【技术特征摘要】
1.一种聚羧酸高效减水剂，生产该产品使用的原料按重量配比包括：丙烯酸8%-9%、甲基丙烯酸钠2%-3%、马来酸酐4%、过硫酸钠2%、氢氧化钙3%、去离子水80%，其特征是：（1）用5个搅拌容器分别将配方量的丙烯酸、甲基丙烯酸钠、马来酸酐、过硫酸钠、氢氧化钙配制成浓度20%的水溶液；（2）将丙烯酸、甲基丙烯酸钠、马来酸酐、过硫酸钠、氢氧化钙的20%水溶液同时送入化学反应釜，开...