The invention relates to the field of air conditioning pipes, in particular to a preparation method of a new type of air conditioning pipes. The preparation method comprises: (a) putting nylon particles into the drying equipment for drying at a drying temperature of 80 90 degrees and a drying time of more than 80 minutes; (b) heating the extruder to 200 220 degrees, then putting the dried nylon particles into the extruder and extruding them with the screw of the extruder to form raw materials; (c) extruding the raw materials through the required diameter die. Press into nylon pipe; (d) inspect nylon pipe; (e) cool nylon pipe to solidify it; (f) cut the solidified nylon pipe. The invention can process nylon particles into air-conditioning pipes, thereby reducing the weight and cost of air-conditioning pipes.
【技术实现步骤摘要】
新型空调管材的制备方法
本专利技术涉及空调管材领域，尤其是新型空调管材的制备方法。
技术介绍
随着对汽车节能要求的提升和汽车零部件技术的不断进步，为了降低汽车油耗，对汽车零件的重量要求也越来越高，需要逐步向轻量化发展。空调管的材料发展从前期的钢管发展到后来的铜管，再然后发展到采用铝管，目前的空调管采用的材料是铝管、胶管、SPCC材料支架的混合体，合并在一起后重量比较重，且成本比较高。
技术实现思路
为了克服现有的空调管材重量重且成本高的不足，本专利技术提供了新型空调管材的制备方法。本专利技术解决其技术问题所采用的技术方案是：一种新型空调管材的制备方法，该制备方法为：（a）、将尼龙颗粒放入烘干设备内进行烘干，烘干温度为80-90度，烘干时间为80分钟以上；（b）、将挤出机加热至200-220度，然后将烘干好的尼龙颗粒放入到挤出机中，利用挤出机的螺杆进行挤压而成为原料；（c）、原料通过需要的管径模具而挤压成尼龙管；（d）、对尼龙管进行检测；（e）、对尼龙管进行冷却使之固化；（f）、将固化好的尼龙管进行切割。根据本专利技术的另一个实施例，进一步包括步骤（a）中，所述烘干时间...
【技术保护点】
1.一种新型空调管材的制备方法，其特征是，该制备方法为：（a）、将尼龙颗粒放入烘干设备内进行烘干，烘干温度为80‑90度，烘干时间为80分钟以上；（b）、将挤出机加热至200‑220度，然后将烘干好的尼龙颗粒放入到挤出机中，利用挤出机的螺杆进行挤压而成为原料；（c）、原料通过需要的管径模具而挤压成尼龙管；（d）、对尼龙管进行检测；（e）、对尼龙管进行冷却使之固化；（f）、将固化好的尼龙管进行切割。
【技术特征摘要】
1.一种新型空调管材的制备方法，其特征是，该制备方法为：（a）、将尼龙颗粒放入烘干设备内进行烘干，烘干温度为80-90度，烘干时间为80分钟以上；（b）、将挤出机加热至200-220度，然后将烘干好的尼龙颗粒放入到挤出机中，利用挤出机的螺杆进行挤压而成为原料；（c）、原料通过需要的管径模具而挤压成尼龙管；（d）、对尼龙管进行检测；（e）、对尼龙管进行冷却使...