一种民用LED凸镜的工艺方法技术

本发明专利技术公开了一种民用LED凸镜的工艺方法，该工艺包括：将聚甲基丙烯酸甲脂置于特制注塑机中，在200‑250℃条件下进行融化处理，之后在所述特制模具中于60‑90℃的条件下分别独立成型，形成所述民用LED凸镜，所述特制模具设有两个(两个以上)模腔。本发明专利技术提供的民用LED凸镜的工艺方法，该方法采用特制机器，在同型号的机器，只曾加一个射台，再特制模具，使生产效率翻一倍（与使用多腔模具的产品相比），提高了民用LED凸镜的生产效率，可广泛的应用于民用LED凸镜领域。

A Processing Method of Civil LED Convex Mirror

The invention discloses a process for civil LED convex mirror. The process includes: placing polymethylmethacrylate in a special injection moulding machine, melting at 200 250 C, then forming the civil LED convex mirror independently at 60 90 C in the special mould, which has two (more) die cavities. The process method of the civil LED convex mirror provided by the invention adopts a special machine, which only adds a shooting platform to the same type of machine, and then makes a special die to double the production efficiency (compared with the products using multi-cavity dies), improves the production efficiency of the civil LED convex mirror, and can be widely used in the field of civil LED convex mirror.

【技术实现步骤摘要】
一种民用LED凸镜的工艺方法
本专利技术涉及一种民用LED凸镜的工艺方法，属于注塑领域。
技术介绍
目前民用LED凸镜应用广、需求量大，但是产品质量不高，生产效率很低，且行业竞争激烈，这些问题已严重阻碍行业的发展。
技术实现思路
本专利技术的目的在于提供一种民用LED凸镜的工艺方法，以克服现有技术中的不足。为实现前述专利技术目的，本专利技术采用的技术方案包括：本专利技术实施例提供一种民用LED凸镜的工艺方法，其包括以下步骤：将聚甲基丙烯酸甲脂置于特制注塑机中，在200-250℃条件下进行融化处理，之后在所述特制模具中于60-90℃的条件下分别独立成型，形成所述民用LED凸镜，所述特制模具设有两个模腔。进一步的，所述特制模具的两个模腔重叠。进一步的，所述特制机器中设有两个专用熔胶筒组件。进一步的，所述特制机器中设有A专用熔胶筒组件和B专用熔胶筒组件，所述特制模具设有A模腔和B模腔，且所述A专用熔胶筒组件对A模腔注塑，所述B专用熔胶筒组件对B模腔注塑。进一步的，所述特制机器的A专用熔胶筒组件安装在动模板上。进一步的，所述特制机器的B专用熔胶筒组件安装在动模板上。与现有技术相比，本专利技术的优本文档来自技高网...

【技术保护点】
1.一种民用LED凸镜的工艺方法，其特征在于包括以下步骤：将聚甲基丙烯酸甲脂置于特制注塑机中，在200‑250℃条件下进行融化处理，之后在所述特制模具中于60‑90℃的条件下分别独立成型，形成所述民用LED凸镜，所述特制模具设有两个(两个以上)模腔。

【技术特征摘要】
1.一种民用LED凸镜的工艺方法，其特征在于包括以下步骤：将聚甲基丙烯酸甲脂置于特制注塑机中，在200-250℃条件下进行融化处理，之后在所述特制模具中于60-90℃的条件下分别独立成型，形成所述民用LED凸镜，所述特制模具设有两个(两个以上)模腔。2.根据权利要求1所述的民用LED凸镜的工艺方法，其特征在于：所述特制模具的两个模腔重叠。3.根据权利要求1所述的民用LED凸镜的工艺方法，其特征在于：所述特制...

【专利技术属性】
技术研发人员：杨国松，张贻刚，张贻青，
申请(专利权)人：苏州路熙光电科技有限公司，
类型：发明
国别省市：江苏,32