本发明专利技术公开了一种钢筋连接用套筒灌浆料，涉及混凝土技术领域，解决了现有的灌浆料容易产生裂缝的技术问题。其包括如下重量份数的组分：硅酸盐水泥500‑530份；石英砂430‑470份；CSA膨胀剂0.1‑0.5份；微珠25‑30份；聚羧酸减水剂1.5‑2.5份；消泡剂0.3‑0.4份。本发明专利技术采用微珠和聚羧酸减水剂提高灌浆料的和易流动性和自抗强度，采用膨胀剂形成均匀致密的泡孔，消除灌浆料收缩时的应力，避免产生裂缝。

Sleeve grouting material for steel bar connection

The invention discloses a sleeve grouting material for reinforcing bar connection, which relates to the technical field of concrete, and solves the technical problem that the existing grouting material is prone to cracks. It consists of 500 530 Portland cement, 430 470 quartz sand, 0.1 0.5 CSA expansive agent, 25 30 microspheres, 1.5 2.5 Polycarboxylic Water Reducer and 0.3 0.4 defoamer. The invention adopts micro-beads and polycarboxylic acid water reducer to improve the fluidity and self-resistance strength of grouting material, adopts expansion agent to form uniform and compact bubbles, eliminates the stress during shrinkage of grouting material and avoids cracking.

【技术实现步骤摘要】
钢筋连接用套筒灌浆料
本专利技术涉及混凝土
，更具体地说，它涉及钢筋连接用套筒灌浆料。
技术介绍
灌浆料是以高强度材料作为骨料，以水泥作为结合剂，辅以高流态、微膨胀、防离析等物质配制而成。它在施工现场加入一定量的水，搅拌均匀后即可使用。灌浆料具有自流性好，快硬、早强、高强、无收缩、微膨胀；无毒、无害、不老化、对水质及周围环境无污染，自密性好、防锈等特点。在施工方面具有质量可靠，降低成本，缩短工期和使用方便等优点。从根本上改变设备底座受力情况，使之均匀地承受设备的全部荷载，从而满足各种机械，电器设备(重型设备高精度磨床)的安装要求，是无垫安装时代的理想灌浆材料。在专利号为CN201710644644.8的中国专利技术专利中公开了一种新型灌浆料，包括如下重量份的原料：废弃混凝土20～30份、水泥10～20份、矿粉8～15份、铁尾矿矿渣15～25份、粉煤灰10～30份、骨料7～22份、废弃石子5～10份、废石膏6～12份、聚丙烯纤维3～6份、羟丙基纤维素2～3份、纳米水化硅酸钙1～2份、膨胀剂3～8份、消泡剂2～3份、减水剂0.5～1份、早强剂2～6份、防沉剂0.3～0.7份、引气剂本文档来自技高网...

【技术保护点】
1.钢筋连接用套筒灌浆料，其特征在于，包括如下重量份数的组分：硅酸盐水泥500‑530份；石英砂430‑470份；CSA膨胀剂0.1‑0.5份；微珠25‑30份；聚羧酸减水剂1.5‑2.5份；消泡剂0.3‑0.4份。

【技术特征摘要】
1.钢筋连接用套筒灌浆料，其特征在于，包括如下重量份数的组分：硅酸盐水泥500-530份；石英砂430-470份；CSA膨胀剂0.1-0.5份；微珠25-30份；聚羧酸减水剂1.5-2.5份；消泡剂0.3-0.4份。2.根据权利要求1所述的钢筋连接用套筒灌浆料，其特征在于，所述钢筋连接用套筒灌浆料还包括1-3份的复合缓凝剂。3.根据权利要求2所述的钢筋连接用套筒灌浆料，其特征在于，所述复合缓凝剂包括缓凝剂A和缓凝剂B，所述缓凝剂A选自二聚磷酸盐、硝基木质素、氧化锌中的任意一种；所述缓凝剂B选自乳酸、酒石酸、柠檬酸中的任意一种。4.根据权利要求3所述的钢筋连接用套筒灌浆料，其特征在于，所述钢筋连接用套...