The invention discloses a heat-resistant and corrosion-resistant paint for transformer shell, which is composed of five parts of phenolic resin, six parts of fluorocarbon resin, six parts of iron oxide red, three parts of immortal red, four parts of catechol, six parts of zinc sulfate, three parts of dimethylsiloxane, and modified epoxy polymer according to the weight of raw materials as follows: 5 parts of phenolic resin, 6 parts of fluorocarbon resin, 6 parts of iron oxide red, 3 parts of immortal red, 4 parts of catechol, 18 parts of zinc sulfate, 3 parts of dimethylsiloxane and 13 parts of modified EP Ammonium polyacrylate 5_15, ammonium polyacrylate 4_16, siloxane 2_18, methanol 4_16, zinc oxide 4_18, mineral oil 6_18. The invention has the advantages of high temperature resistance, oxidation resistance and low cost.
【技术实现步骤摘要】
一种耐高温防腐蚀变压器外壳用漆
本专利技术涉及一种保护漆，尤其涉及一种耐高温防腐蚀变压器外壳用漆。
技术介绍
目前，随着工业水平的发展，变压器作为工业中常用的设备被人们广泛使用，但是变压器外壳的保存不能够长久，很容易被空气中的氧气所氧化，人们通常采用在变压器外壳表面涂覆一层保护漆的方式达到保护变压器的目的，但是现有人们所使用的保护漆不能够有效的保护变压器，很容易出现被氧化的情况，不利于人们的使用。
技术实现思路
为了克服上述现有技术的缺陷，本专利技术的目的是提供一种耐高温防腐蚀变压器外壳用漆。本专利技术是采取以下技术方案来实现的：一种耐高温防腐蚀变压器外壳用漆，由以下按照重量份数的原料组成：酚醛树脂5-25份、氟碳树脂6-18份、氧化铁红粉6-18份、永固红3-13份、邻苯二酚4-18份、硫酸锌6-18份、二甲基硅氧烷3-13份、改性环氧聚氨酯5-15份、聚丙烯酸铵4-16份、硅氧烷2-18份、甲醇4-16份、氧化锌4-18份、矿物油6-18份。上述的一种耐高温防腐蚀变压器外壳用漆，由以下按照重量份数的原料组成：酚醛树脂5-23份、氟碳树脂6-16份、氧化铁红粉6-1...
【技术保护点】
1.一种耐高温防腐蚀变压器外壳用漆，其特征在于，由以下按照重量份数的原料组成：酚醛树脂5‑25份、氟碳树脂6‑18份、氧化铁红粉6‑18份、永固红3‑13份、邻苯二酚4‑18份、硫酸锌6‑18份、二甲基硅氧烷3‑13份、改性环氧聚氨酯5‑15份、聚丙烯酸铵4‑16份、硅氧烷2‑18份、甲醇4‑16份、氧化锌4‑18份、矿物油6‑18份。
【技术特征摘要】
1.一种耐高温防腐蚀变压器外壳用漆，其特征在于，由以下按照重量份数的原料组成：酚醛树脂5-25份、氟碳树脂6-18份、氧化铁红粉6-18份、永固红3-13份、邻苯二酚4-18份、硫酸锌6-18份、二甲基硅氧烷3-13份、改性环氧聚氨酯5-15份、聚丙烯酸铵4-16份、硅氧烷2-18份、甲醇4-16份、氧化锌4-18份、矿物油6-18份。2.根据权利要求1所述的一种耐高温防腐蚀变压器外壳用漆，其特征在于，由以下按照重量份数的原料组成：酚醛树脂5-23份、氟碳树脂6-16份、氧化铁红粉6-16份、...