The present invention relates to a method of preparing color material by using manganese carbonate, which carries out surface modification treatment of manganese carbonate, and then carries out aging treatment of manganese carbonate after surface modification at 30 50 (?) C. The time of aging treatment is 48 60 h, and then mixes manganese carbonate after aging treatment with auxiliary raw materials to form a mixture. The mixture is calcined at a heating rate of 80 100 (?) C/h from 0 (?) C to 1150 (?) C, and then the calcined mixture is heated at 1130 1200 (?) C for 1 2 h to obtain the color. The method of preparing color by using manganese carbonate has the advantages of widening the firing range of the prepared color and good high temperature performance, and can be applied to high-end ceramic products.
【技术实现步骤摘要】
一种可使色料色调鲜艳的利用碳酸锰制备色料的方法本案是以申请日为2016年02月29日，申请号为201610111336.4，名称为“一种利用碳酸锰制备色料的方法”的专利技术专利为母案而进行的分案申请。
本专利技术涉及色料生产工艺，特别涉及一种利用碳酸锰制备色料的方法。
技术介绍
目前陶瓷色料行业中采用碳酸锰为原料以生产色料。该色料多为桃红色色料，现有技术中的采用碳酸锰为原料生产桃红色色料的方法存在色料烧成范围窄、在1250℃以上温度环境下使用时釉面容易出现针孔、着色力弱和色调不够鲜艳的问题，即存在高温环境下使用效果不佳的不足。因而无法应用于高端的陶瓷制品中。专利号为200710106267.9的中国专利技术专利公开了一种锰掺杂刚玉型粉红色料的制备方法，其步骤为：(1)将所需硝酸铝、氢氧化铝、硝酸锰和碳酸锰四种原料按摩尔比Mn∶Al＝0.15～0.20的比例计算出所用各原料的质量，将其配入体积比为30∶70的乙醇和水的溶液中；(2)将配制好的混合溶液放入和喷枪进液管连接的容器内，并进行强烈搅拌，在喷枪的进气口接入0.3～0.8kg/cm2压力的压缩空气；(3)在连续...
【技术保护点】
1.一种可使色料色调鲜艳的利用碳酸锰制备色料的方法，其特征在于，将碳酸锰进行表面改性处理，然后将表面改性处理后的碳酸锰于40℃条件下进行陈腐处理，所述陈腐处理的时间为55h，然后将陈腐处理后的碳酸锰与辅助原料混合，形成混合物，将所述混合物以90℃/h的升温速率由0℃煅烧至1150℃，然后将煅烧后的混合物于1180℃条件下保温1.5h，将保温后的混合物依次进行研磨、水洗和烘干，获得所述色料；所述碳酸锰的粒度为11μm；将陈腐处理后的碳酸锰于温度为135℃条件下烘干240min，再将陈腐处理后的碳酸锰的研磨至碳酸锰的粒度为4μm，再与辅助原料混合；所述辅助原料为氧化铝、氢氧化铝、磷酸钙或氯化钙。
【技术特征摘要】
1.一种可使色料色调鲜艳的利用碳酸锰制备色料的方法，其特征在于，将碳酸锰进行表面改性处理，然后将表面改性处理后的碳酸锰于40℃条件下进行陈腐处理，所述陈腐处理的时间为55h，然后将陈腐处理后的碳酸锰与辅助原料混合，形成混合物，将所述混合物以90℃/h的升温速率由0℃煅烧至1150℃，然后将煅烧后的...
【专利技术属性】
技术研发人员：李小毅，叶旦旺，程诗忠，包晓刚，范志强，
申请(专利权)人：三祥新材股份有限公司，
类型：发明
国别省市：福建,35