The invention discloses an insulating and fireproof board, which is composed of the following raw materials: styrene 200 260, diisopropylbenzene peroxide 6 8, tributyl phosphate 13 20, melamine 3 5, sucrose acetate 0.1 0.3, bisphenol A2 4, methyl methacrylate 20 30, ammonium persulfate 1 2, acrylic acid 10. 15, antimony trioxide 10 18 and nano-silica 20 30. The present invention takes styrene as the monomer, through polymerization, effectively improves the dispersion compatibility of nano-silica among finished products, and improves the mechanical properties of finished products. The melamine phosphate and bisphenol A polyester introduced by the present invention can play a good synergistic flame retardant role. The fireproof property of the finished product is improved.
【技术实现步骤摘要】
一种保温防火板材及其制备方法
本专利技术属于防火材料领域，具体涉及一种保温防火板材及其制备方法。
技术介绍
聚苯乙烯泡沫材料是以聚苯乙烯树脂为基料，加入发泡剂等辅助材料，经加热发泡而成的轻质材料，它具有质轻、导热系数小、吸水率低、耐水、耐老化、耐低温、易加工、价廉质优等优点。但是聚苯乙烯泡沫保温材料在给人们的生活带来巨大方便的同时，其易燃性也给它的应用带来了一定的限制。聚苯乙烯泡沫本身是易燃材料，在火灾和高温条件下极易发生分解燃烧，并伴有大量毒气产生；因此，急需研究一种新的聚苯乙烯泡沫保温材料，以提高火灾安全性。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种保温防火板材及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种保温防火板材，它是由下述重量份的原料组成的：苯乙烯200-260、过氧化二异丙苯6-8、磷酸三丁酯13-20、三聚氰胺3-5、乙酸异丁酸蔗糖酯0.1-0.3、双酚A2-4、甲基丙烯酸甲酯20-30、过硫酸铵1-2、丙烯酸10-15、三氧化二锑10-18、纳米二氧化硅20-30。所述的催化剂为对甲基苯磺酸。一种保温防火板...
【技术保护点】
1.一种保温防火板材，其特征在于，它是由下述重量份的原料组成的：苯乙烯200‑260、过氧化二异丙苯6‑8、磷酸三丁酯13‑20、三聚氰胺3‑5、乙酸异丁酸蔗糖酯0.1‑0.3、双酚A2‑4、甲基丙烯酸甲酯20‑30、过硫酸铵1‑2、丙烯酸10‑15、三氧化二锑10‑18、纳米二氧化硅20‑30。
【技术特征摘要】
1.一种保温防火板材，其特征在于，它是由下述重量份的原料组成的：苯乙烯200-260、过氧化二异丙苯6-8、磷酸三丁酯13-20、三聚氰胺3-5、乙酸异丁酸蔗糖酯0.1-0.3、双酚A2-4、甲基丙烯酸甲酯20-30、过硫酸铵1-2、丙烯酸10-15、三氧化二锑10-18、纳米二氧化硅20-30。2.根据权利要求1所述的一种保温防火板材，其特征在于，所述的催化剂为对甲基苯磺酸。3.一种如权利要求1、2中任一所述保温防火板材的制备方法，其特征在于，包括以下步骤：(1)取过硫酸铵，加入到其重量20-30倍的去离子水中，搅拌均匀；(2)取甲基丙烯酸甲酯、丙烯酸、三氧化二锑混合，加入到混合料重量5-8倍的去离子水中，搅拌均匀，送入到反应釜中，通入氮气，调节反应釜温度为50-65℃，加入上述过硫酸铵水溶液，保温搅拌3-5小时，抽...