The invention belongs to the technical field of polymer composite synthesis, in particular to a high mechanical strength GO/TPU in-situ polymerization method. The process of in-situ polymerization is as follows: graphene oxide, polypropylene glycol 4000, toluene diisocyanate and 1,4 butanediol are used as raw materials to modify graphene oxide with glacial acetic acid and dialkyl dimethyl ammonium bromide, and then combined with polypropylene glycol 4000 to form modified graphene oxide/polypropylene glycol 4000. GO/TPU with high mechanical strength was obtained by in-situ polymerization of the blend with toluene diisocyanate and 1,4 -butanediol. The GO/TPU material prepared by the method of the invention has excellent mechanical strength and can become a better substitute in mechanical industry and other fields.
【技术实现步骤摘要】
一种高力学强度GO/TPU原位聚合方法
本专利技术属于高分子复合材料合成
，具体涉及一种高力学强度GO/TPU原位聚合方法。
技术介绍
高分子材料因其良好的性能已广泛应用于各种领域，特别是在机械工业等需要众多结构材料的领域中。用性能良好、质轻、加工便利的高分子材料去替代金属、木材、陶瓷等已成为了现今材料领域的研究热门。具有高力学强度的高分子材料拓宽了材料的选用范围，使传统机械产品逐步完成了从高消耗、高质量向轻便、耐腐蚀、低成本的转变。热塑性聚氨酯弹性体简称TPU，又称PU热塑胶，是一种由低聚物多元醇软段与二异氰酸酯、扩链剂硬段构成的线性嵌段共聚物。TPU分子中同时含有柔性软链段和刚性硬链段，软段使TPU具有较好的弹性、柔顺性及耐寒性，硬段则使得TPU具有较高的硬度、弹性模量和热稳定性。硬段分子间氢键以及大分子间的轻度交联使得TPU存在强物理交联结构，具有较强的物理强度，同时TPU加工性能良好，这使得TPU在汽车部件及机器零件、运动鞋底、电线电缆、软管、薄膜及薄板、织物、建筑、食品包装等领域有着广泛的应用前景。但在力学强度需求较高的领域中，现有方法合成的TPU...
【技术保护点】
1.一种高力学强度GO/TPU原位聚合方法，其特征在于：所述GO/TPU的原料按重量份数计包括：0.05~0.1份氧化石墨烯，60.0份聚丙二醇‑4000，27.4份甲苯二异氰酸酯，12.6份1,4‑丁二醇；所述甲苯二异氰酸酯为TDI‑80；氧化石墨烯使用前依次用冰乙酸、双十烷基二甲基溴化铵处理，其中，冰乙酸过量，氧化石墨烯与双十烷基二甲基溴化铵质量比为3：1。
【技术特征摘要】
1.一种高力学强度GO/TPU原位聚合方法，其特征在于：所述GO/TPU的原料按重量份数计包括：0.05~0.1份氧化石墨烯，60.0份聚丙二醇-4000，27.4份甲苯二异氰酸酯，12.6份1,4-丁二醇；所述甲苯二异氰酸酯为TDI-80；氧化石墨烯使用前依次用冰乙酸、双十烷基二甲基溴化铵处理，其中，冰乙酸过量，氧化石墨烯与双十烷基二甲基溴化铵质量比为3：1。2.根据权利要求1所述的一种高力学强度GO/TPU原位聚合方法，其特征在于：采用冰乙酸及双十烷基二甲基溴化铵对氧化石墨烯进行改性后，与聚丙二醇-4000结合形成改性氧化石墨烯/聚丙二醇-4000共混物，再与甲苯二异氰酸酯、1,4-丁二醇原位聚合得到高力学强度的GO/TPU。3.根据权利要求2所述的一种高力学强度GO/TPU原位聚合方法，其特征在于：包括以下步骤：1）氧化石墨烯的制备：以鳞片石墨为原料，采用改进的Hummers法制备氧化石墨烯；2）改性氧化石墨烯的制备：向氧化石墨烯中倒入冰乙酸，超声振荡3~4h，...