The invention discloses a flotation method for fine cassiterite, which belongs to the technical field of mineral processing. The method of the invention adopts the composition of sodium carbonate, sodium tripolyphosphate and sodium humate as flocculant, the composition of oleic acid and citric acid as collector, and the mass percentage concentration of sodium carbonate in the flocculant is 2-10 wt%, the mass percentage concentration of sodium tripolyphosphate is 20-70 wt%, and the mass percentage concentration of sodium humate is 20%. The concentration of oleic acid and citric acid in the collector is 10-90 wt% and 10-90 wt% respectively. The combined flocculant and collector in the method has the advantages of good selectivity, low consumption of reagents, low price, solubility at room temperature, non-toxicity, high efficiency and environmental protection, especially for the flotation of minute cassiterite with a good effect, which is of great significance for improving the recovery and utilization of tin resources.
【技术实现步骤摘要】
一种微细粒锡石浮选方法
本专利技术涉及一种微细粒锡石浮选方法，属于矿物加工
技术介绍
锡的主要原料为锡石，锡石是一种密度较大、质脆的矿物，在开采过程中容易破碎成细小颗粒。鉴于锡石密度较大的特点，重选为锡石的传统选矿工艺。但大部分锡矿石的成分复杂、可回收有价组分较多，采用单一重选法很难获得良好的锡分选指标和有效回收其他有价金属组分，故需采用重、磁、电等物理选矿方法与浮选、焙烧、浸出等化学选矿方法联合，提高锡矿石中锡和其他有价组分的回收率。对于大颗粒锡石，一般采用重选法回收；而对于微细粒锡石，重选回收率低，一般采用浮选法或联合法回收。对于微细粒锡石的浮选一直是一个世界性的难题，主要是崁布粒度细，难以实现颗粒的单体解离，浮选中要把矿石磨得很细才能进行浮选，然而粒度太细矿物颗粒的表面能较大，捕收剂难以在矿粒表面吸附。
技术实现思路
本专利技术针对现有微细粒锡石浮选效果差的问题，提供了一种微细粒锡石浮选方法，该方法对-20μm的微细粒锡石浮选具有较好选择性，可以获得较好的锡石回收指标；采用该组合药剂具有捕收能力强、选择性好的特点，浮选时只需要添加少量的抑制剂就可以取得...
【技术保护点】
1.一种微细粒锡石的浮选方法，其特征在于：选用碳酸钠、三聚磷酸钠、腐殖酸钠的组合物作为絮凝剂，油酸和柠檬酸的组合物作为捕收剂，絮凝剂中碳酸钠的质量百分比浓度为2~10wt%、三聚磷酸钠的质量百分比浓度为20~70wt%、腐殖酸钠的质量百分比浓度为20~70wt%，捕收剂中油酸的质量百分比浓度为10~90wt%、柠檬酸的质量百分比浓度为10~90wt%。
【技术特征摘要】
1.一种微细粒锡石的浮选方法，其特征在于：选用碳酸钠、三聚磷酸钠、腐殖酸钠的组合物作为絮凝剂，油酸和柠檬酸的组合物作为捕收剂，絮凝剂中碳酸钠的质量百分比浓度为2~10wt%、三聚磷酸钠的质量百分比浓度为20~70wt%、腐殖酸钠的质量百分比浓度为20~70wt%，捕收剂中油酸的质量百分比浓度为10~90wt%...