本发明专利技术公开了一种铜冶炼炉渣高细度浮选铜精矿沉降方法，在精矿浆沉淀时，加入非离子聚丙烯酰胺和聚合氯化铝，由于铜精矿粒度较细，铜精矿悬浮在精矿浓缩池上部分，难以澄清分离，采用本发明专利技术絮凝剂沉降分离的方法，使铜精矿在精矿浓缩池内快速沉降，达到铜精矿溢流水与铜精矿快速澄清分离，精矿浓缩池溢流水“跑浑”现象得到解决，渣选磨浮工序得以连续生产。

A copper smelting furnace slag and high fineness flotation copper concentrate settlement method

The invention discloses a copper smelting slag of high fineness floatation copper concentrates in the concentrate slurry settling method, precipitation, adding non-ionic polyacrylamide and polyaluminium chloride, the copper concentrate size is fine, suspension concentrates in copper concentrate pool, to clarify the separation, adopting the method of flocculant sedimentation separation, the copper concentrate rapid subsidence in concentrates in the pool, to overflow and copper concentrate copper concentrate fast separation, concentrate thickener overflow \mudflow\ phenomenon is solved, the slag grinding flotation process can be selected for continuous production.

【技术实现步骤摘要】
一种铜冶炼炉渣高细度浮选铜精矿沉降方法
本专利技术涉及铜冶炼
，具体是一种铜冶炼炉渣高细度浮选铜精矿沉降方法。
技术介绍
申请人针对铜冶炼渣选系统经过多次试车发现，存在炉渣比重较大（4.1吨/立方左右）、硬度较硬（莫氏硬度7～9度）。为了取得较好的选矿技术指标，必须使有用矿物单体解离，提高入选矿浆浓细度（≦-325目，0.045mm大于70%以上），确保有用矿物的可浮性。但最终导致浮选产品铜精矿粒度非常细，经过筛分实验铜精矿85%含量小于（-325目，0.045mm），具体筛分数据如下表（铜精矿粒级组成）：
技术实现思路
为解决上述问题，本专利技术提供一种铜冶炼炉渣高细度浮选铜精矿沉降方法，使铜精矿在精矿浓缩池内快速沉降，达到铜精矿溢流水与铜精矿快速澄清分离。本专利技术通过下列技术方案实现：一种铜冶炼炉渣高细度浮选铜精矿沉降方法，在精矿浆沉淀时，加入非离子聚丙烯酰胺PMC和聚合氯化铝PAC。优选的，所述非离子聚丙烯酰胺和聚合氯化铝在常温下混合配成溶液，通过搅拌加入。优选的，所述非离子聚丙烯酰胺加入量为0.500g/l-2.00g/l：所述聚合氯化铝加入量为2.50g/l-5.00g本文档来自技高网...

【技术保护点】
一种铜冶炼炉渣高细度浮选铜精矿的沉降方法，其特征在于，在精矿浆沉淀时，加入非离子聚丙烯酰胺和聚合氯化铝。

【技术特征摘要】
1.一种铜冶炼炉渣高细度浮选铜精矿的沉降方法，其特征在于，在精矿浆沉淀时，加入非离子聚丙烯酰胺和聚合氯化铝。2.根据权利要求1所述的一种铜冶炼炉渣高细度浮选铜精矿沉降方法，其特征在于，所述非离子聚丙烯酰胺和聚合氯化铝在常温下混合配成溶液，通过搅拌加入。3.根据权利要求1或2所述的一种铜冶炼炉渣高细度浮选铜精矿沉降方法，其特征在于，所述非离子聚丙烯酰胺加入量为0.500g/l-2.00g/l：所述聚合氯化铝加入...