The invention discloses a method for preparing paper-making retention aid from low-grade attapulgite, which takes low-grade attapulgite as main material and according to the mass percentage, the content of attapulgite is 20 30%, montmorillonite is 10 30%, dolomite is 10 30%, quartz or opal is less than 10%, and the rest is other types of clay. Attapulgite ore is blended to reach the above proportion range. After repeated water spraying, static setting and roller extrusion treatment for 3 to 4 times, it is dried and crushed, and 5 to 10% organic retention aid is added. Paper retention aid can be obtained by uniform mixing. The invention integrates three functions of filling, retention and filtration, realizes high value application of concave soil while saving energy, reducing consumption, cleaning production and improving paper quality.
【技术实现步骤摘要】
低品位凹土制备造纸助留剂的方法
本专利技术涉及低品位凹土深加工及其作为造纸助留剂的加工方法，属于非金属矿物资源利用
技术介绍
凹凸棒土、膨润土、高岭土、碳酸钙、硅灰石、滑石等非金属矿物在造纸领域有着广泛的应用，例如，专利号为200410049606.0，名称为“造纸矿物复合助留剂及其制备方法与应用”公开了将膨润土、方解石、硅灰石、海泡石、凹凸棒土、沸石和高岭土矿物提纯并煅烧研磨，然后在加入一定比例的硅灰石和海泡石搅拌均匀得到。申请号为201210013223.2，名称为“阳离子造纸复合助留剂及其制备方法和应用方法”公开了将膨润土、方解石、硅灰石、海泡石、凹凸棒石、沸石、水滑石和高岭土混合并经煅烧研磨后得到。申请号为201410365287.8，名称为“造纸助留剂及其制备方法”公开了将膨润土、方解石、凹凸棒土、硅灰石、滑石按比例混合研磨，以壳聚糖、聚丙烯酰胺和冰醋酸预处理得高分子组分与上述混合物进一步按比例混合得到。从上述三件公开的内容可知，现有技术制备的助留剂均涉及多种非金属矿物的复配，但均未考虑天然非金属矿成分的复杂性和多变性；其次专利号2004100...
【技术保护点】
1.低品位凹土制备造纸助留剂的方法，其特征在于：该助留剂以低品位凹土为主料，按质量百分比，其中凹凸棒石含量为20‑30%，蒙脱石含量为10‑30%，白云石含量为10‑30%，石英或蛋白石含量≤10%,余为其它类型黏土；首先根据需要对凹土矿进行配矿以使其达到上述比例范围，再经重复喷水静置和对辊挤压处理3‑4次后，晒干并粉碎，加5‑10%有机助留剂，搅拌均匀即得造纸助留剂。
【技术特征摘要】
1.低品位凹土制备造纸助留剂的方法，其特征在于：该助留剂以低品位凹土为主料，按质量百分比，其中凹凸棒石含量为20-30%，蒙脱石含量为10-30%，白云石含量为10-30%，石英或蛋白石含量≤10%,余为其它类型黏土；首先根据需要对凹土矿进行配矿以使其达到上述比例范围，再经重复喷水静置和对辊挤压处理3-4次后，晒干并粉碎，加5-10%有机助留剂，搅拌均匀即得造纸助留剂。2.根据权利要求1所述的低品位凹土制备造纸...
【专利技术属性】
技术研发人员：陈静，金叶玲，吴剑，倪伶俐，蒋金龙，
申请(专利权)人：淮阴工学院，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。