The invention discloses a wrinkle resistant blended fabric, which comprises a base cloth layer and a wrinkle resistant layer. The baseboard layer is made of warp and weft, silk fibers are used for warp and bamboo charcoal fibers for weft, of which the size of silk fibers is 218 dtex and the warp density is 46.2 dtex; the size of bamboo charcoal fibers is 142 dtex and the weft density is 93.8 dcm; the wrinkle resistant layer includes Pearl fibers, soybean protein fibers and Modal fibers. Initiator and accelerator. The invention improves the formula of the existing wrinkle resistant coating, and makes the wrinkle resistance of the prepared wrinkle resistant blended fabric superior to the existing similar products.
【技术实现步骤摘要】
一种抗皱混纺面料
本专利技术涉及一种面料,尤其涉及一种抗皱混纺面料。
技术介绍
现有的面料品种众多,但随着人们生活水平的提高,需要提供能满足不同人群需要的新品种。人们对服装的要求不仅仅对服装款式、做工的要求,更多的是对服装品质的要求,这就要求在服装面料上要跟得上服装形式的发展,功能性、舒适、环保、健康等面料的特征成为人们越来越关注的话题
技术实现思路
2.本专利技术解决其技术问题所采用的技术方案是:一种抗皱混纺面料,其特征是:该面料包括基布层、抗皱层。所述基布层由经线和纬线混纺而成,经线采用蚕丝纤维,纬线采用竹炭纤维,其中蚕丝纤维的纤度为218dtex,经密度为46.2根/cm;竹炭纤维的纤度为142dtex,纬密度为93.8根/cm;所述抗皱层包括珍珠纤维、大豆蛋白纤维、莫代尔纤维、引发剂、促进剂。本专利技术的有益效果是:本专利技术改进了现有抗皱涂层的配方,使其制备的抗皱混纺面料的抗皱性优于现有同类产品。具体实施方式3.具体实施例:一种抗皱混纺面料,其特征是:该面料包括基布层、抗皱层。所述基布层由经线和纬线混纺而成,经线采用蚕丝纤维,纬线采用竹炭纤维,其中蚕丝纤维的纤度为218dtex,经密度为46.2根/cm;竹炭纤维的纤度为142dtex,纬密度为93.8根/cm;所述抗皱层包括珍珠纤维、大豆蛋白纤维、莫代尔纤维、引发剂、促进剂。本专利技术的有益效果是:本专利技术改进了现有抗皱涂层的配方,使其制备的抗皱混纺面料的抗皱性优于现有同类产品。显然,上述实施例仅仅是为清楚地说明所作的举例,而并非对实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上 ...
【技术保护点】
1.一种抗皱混纺面料,其特征是:该面料包括基布层、抗皱层。所述基布层由经线和纬线混纺而成,经线采用蚕丝纤维,纬线采用竹炭纤维,其中蚕丝纤维的纤度为218dtex,经密度为46.2根/cm;竹炭纤维的纤度为142dtex,纬密度为93.8根/cm;所述抗皱层包括珍珠纤维、大豆蛋白纤维、莫代尔纤维、引发剂、促进剂。
【技术特征摘要】
1.一种抗皱混纺面料,其特征是:该面料包括基布层、抗皱层。所述基布层由经线和纬线混纺而成,经线采用蚕丝纤维,纬线采用竹炭纤维,其中蚕丝纤维的纤度为218dt...