The invention discloses a chromium-free passivator for hot-dip galvanizing. The passivator comprises raw materials with the following mass percentages: film-forming agent 5-8%, phosphoric acid 1-1.2%, accelerator 1.2-2.5%, complexing agent 0.8-3% and residual amount of water. The preparation method comprises the following steps: 1. Film-forming agent, accelerator, complexing agent and water are mixed and added into stirring tank. Mixture A was obtained by mixing at a low speed with a stirring rate of 800 rpm and a stirring time of 22 min. Step 2: Phosphoric acid was added to the mixture and then high-speed stirring was added to the stirring tank. Mixture B was obtained at a stirring rate of 5000 rpm and a stirring time of 30 min. Step 3: The mixture B was concentrated in vacuum for 10 min to obtain a chromium-free passivator. . The invention has reasonable composition, no heavy metal elements, good passivation effect, good brightness after passivation, no discoloration, and can pass 72h neutral salt spray experiment.
【技术实现步骤摘要】
热镀锌无铬钝化剂
本专利技术涉及一种钝化剂，特别涉及一种热镀锌无铬钝化剂。
技术介绍
镀锌(包括电镀锌和热浸镀锌)是所有金属表面沉积处理中数量最大的镀种之一，广泛应用于国民经济中的每一个领域，其中镀锌钢板更是汽车工业、电子仪表、家用电器、建筑工业等各个领域的支撑材料。由于锌层自身化学性质活泼，随着使用时间的延长，因遭受环境介质的腐蚀而逐渐失去其对基材的保护作用。对镀锌层进行化学钝化处理是提高镀锌件耐蚀性能最常用的方法。
技术实现思路
本专利技术的目的在于提供一种热镀锌无铬钝化剂。本专利技术采用的技术方案是：热镀锌无铬钝化剂，其特征在于：包括以下质量百分比的原料：成膜剂5～8%、磷酸1～1.2%、促进剂1.2～2.5%、络合剂0.8-3%、余量为水。所述的成膜剂为磷酸二氢钠、磷酸氢钠、偏钒酸铵、硝酸铈和磷钼酸铵中的一种或多种。所述的促进剂为钼酸铵、亚硝酸钠、氯酸钠、硝基苯磺酸钠中的一种或多种。所述的络合剂为葡萄糖酸钠、柠檬酸钠、酒石酸钾钠、苹果酸钠、乙二胺四乙酸二钠中的一种或多种。所述的一种热镀锌无铬钝化剂的制备方法，其特征在于：包括以下步骤：步骤1：将成膜剂、促进剂、...
【技术保护点】
1.热镀锌无铬钝化剂，其特征在于：包括以下质量百分比的原料：成膜剂5～8%、磷酸1～1.2%、促进剂1.2～2.5%、络合剂0.8‑3%、余量为水。
【技术特征摘要】
1.热镀锌无铬钝化剂，其特征在于：包括以下质量百分比的原料：成膜剂5～8%、磷酸1～1.2%、促进剂1.2～2.5%、络合剂0.8-3%、余量为水。2.根据权利要求1所述的热镀锌无铬钝化剂，其特征在于：所述的成膜剂为磷酸二氢钠、磷酸氢钠、偏钒酸铵、硝酸铈和磷钼酸铵中的一种或多种。3.根据权利要求1所述的热镀锌无铬钝化剂，其特征在于：所述的促进剂为钼酸铵、亚硝酸钠、氯酸钠、硝基苯磺酸钠中的一种或多种。4.根据权利要求1所述的热镀锌无铬钝化剂，其特征在于：所...