The invention discloses a wear resistant topcoat for mining equipment. According to the mass fraction, it contains the following raw materials: epoxy acrylate 30, 40, styrene acrylic emulsion 15, 25, silicon powder 2, 5, palm wax 10, 18, turpentine 10, 20, butanol 15, 15, aramid short fiber, 15, alumina, and xylene. Among them, 3_6 were butyl ether, 5_10 were diethylene glycol ether acetate, 20_24 were fluororesin and 6_10 were butyl ester. In the topcoat for mining equipment, styrene acrylic emulsion, silicon micro powder and palm wax are added, which greatly improves the wearing degree of mining equipment, reduces the corrosion phenomenon of mining equipment during use, and prolongs the service life of the equipment.
【技术实现步骤摘要】
一种矿业设备用耐磨面漆
本专利技术涉及矿业设备
，具体涉及一种矿业设备用耐磨面漆。
技术介绍
目前，矿业设备使用的范围内，经常有矿石、矿渣等，矿业设备在使用过程中极易磨损，磨损后的矿业设备容易出现生锈、腐蚀或者变色等现象，严重减少了矿业设备的使用寿命。
技术实现思路
本专利技术的目的在于提供一种矿业设备用耐磨面漆。本专利技术的目的可以通过以下技术方案实现：一种矿业设备用耐磨面漆，按照质量份数计包括如下原料：环氧丙烯酸酯30-40份，苯丙乳液15-25份，硅微粉2-5份，棕榈蜡10-18份，松节油10-20份，丁醇15-25份，芳纶短纤维2-5份，氧化铝10-18份，二甲苯5-10份，丁醚3-6份，二乙二醇乙醚醋酸酯5-10份，氟树脂20-24份和丁酯6-10份。优选的，所述的一种矿业设备用耐磨面漆，按照质量份数计包括如下原料：环氧丙烯酸酯30份，苯丙乳液15份，硅微粉2份，棕榈蜡10份，松节油10份，丁醇15份，芳纶短纤维2份，氧化铝10份，二甲苯5份，丁醚3份，二乙二醇乙醚醋酸酯5份，氟树脂20份和丁酯6份。优选的，所述的一种矿业设备用耐磨面漆，按照质量份数计...
【技术保护点】
1.一种矿业设备用耐磨面漆，其特征在于，按照质量份数计包括如下原料：环氧丙烯酸酯30‑40份，苯丙乳液15‑25份，硅微粉2‑5份，棕榈蜡10‑18份，松节油10‑20份，丁醇15‑25份，芳纶短纤维2‑5份，氧化铝10‑18份，二甲苯5‑10份，丁醚3‑6份，二乙二醇乙醚醋酸酯5‑10份，氟树脂20‑24份和丁酯6‑10份。
【技术特征摘要】
1.一种矿业设备用耐磨面漆，其特征在于，按照质量份数计包括如下原料：环氧丙烯酸酯30-40份，苯丙乳液15-25份，硅微粉2-5份，棕榈蜡10-18份，松节油10-20份，丁醇15-25份，芳纶短纤维2-5份，氧化铝10-18份，二甲苯5-10份，丁醚3-6份，二乙二醇乙醚醋酸酯5-10份，氟树脂20-24份和丁酯6-10份。2.根据权利要求1所述的一种矿业设备用耐磨面漆，其特征在于，按照质量份数计包括如下原料：环氧丙烯酸酯30份，苯丙乳液15份，硅微粉2份，棕榈蜡10份，松节油10份，丁醇15份，芳纶短纤维2份，氧化铝10份，二甲苯5份，丁醚3份，二乙二醇乙醚醋酸酯5份，氟树脂20份和丁酯6份。3.根据权利要求1所述的一种矿业设备用耐磨面漆，其特征在于，按照质量份数计包括如下原料：环氧丙烯酸酯40份，苯丙乳液...
【专利技术属性】
技术研发人员：曹徽，
申请(专利权)人：怀宁县江镇代家凹铜矿有限公司，
类型：发明
国别省市：安徽,34