The invention provides a high efficiency antibacterial coating for ship bottom and a preparation method thereof, relating to the technical field of coating processing. The antimicrobial coating is made of 38 42 parts of epoxy resin, 6 10 parts of nano-titanium dioxide, 8 12 parts of nano-zinc oxide, 12 16 parts of N dodecyl bisquaternary ammonium salt, 4 8 parts of calcium carbonate, 2 6 parts of diatomite, 1.4 2.1 parts of zinc stearate, 6 10 parts of citral and 16 30 parts of xylene. The traditional anti-bacterial coatings have good adhesion to the hull, and can effectively inhibit the growth of algae and microorganisms in seawater. At the same time, they are free of pollutants, safe and environmentally friendly. They are suitable for popularization and use.
【技术实现步骤摘要】
一种船底高效抗菌涂料及其制备方法
本专利技术涉及涂料加工
，具体涉及一种船底高效抗菌涂料及其制备方法。
技术介绍
船舶在大海中航行所遇到的重要难题就是海生物对船底的附着与污损。部分海洋生物是以固定物体附着生长的，水线以下的船底是生物附着的主要基地，海生物附着给船舶航行带来了极大危害。海洋生物的附着会增大船舶对海水的摩擦阻力，造成燃料消耗增加、航速降低。此外，细菌、藻类和微生物等甚至会进一步腐蚀船体，造成损坏，引起严重后果。因此，用于船舶的抗菌涂料是一种特殊涂料，它通过活性成分如杀菌灭藻剂，抑制和阻止细菌、藻类和微生物等海生物在船舶的附着和生长，从而保持船舶外表面光滑和涂层完好，在保证正常航速的前提下，最大限度地降低油耗并延长涂层寿命，减少不必要的维修支出。目前用于船底涂料的树脂基料主要有丙烯酸树脂、丙烯酸树脂衍生物如丙烯酸锌或是丙烯酸铜树脂、沥青以及氯化橡胶。然而，以丙烯酸树脂、丙烯酸树脂衍生物为基料的抗菌涂料，在海水和阳光作用下会产生一定应力，导致抗菌涂料的附着力下降，出现裂纹或部分脱落等力学缺陷，漆膜开裂脱落较为常见。此外丙烯酸树脂衍生物的制作成本较高。...
【技术保护点】
1.一种船底高效抗菌涂料，其特征在于，所述抗菌涂料由以下重量份的原料制成：环氧树脂38‑42份、纳米二氧化钛6‑10份、纳米氧化锌8‑12份、N‑十二烷基双季铵盐12‑16份、碳酸钙4‑8份、硅藻土2‑6份、硬脂酸锌1.4‑2.1份、柠檬醛6‑10份、二甲苯16‑30份。
【技术特征摘要】
1.一种船底高效抗菌涂料，其特征在于，所述抗菌涂料由以下重量份的原料制成：环氧树脂38-42份、纳米二氧化钛6-10份、纳米氧化锌8-12份、N-十二烷基双季铵盐12-16份、碳酸钙4-8份、硅藻土2-6份、硬脂酸锌1.4-2.1份、柠檬醛6-10份、二甲苯16-30份。2.根据权利要求1所述的一种船底高效抗菌涂料，其特征在于，所述抗菌涂料由以下重量份的原料制成：环氧树脂39-41份、纳米二氧化钛7-9份、纳米氧化锌9-11份、N-十二烷基双季铵盐13-15份、碳酸钙5-7份、硅藻土3-5份、硬脂酸锌1.6-1.9份、柠檬醛7-9份、二甲苯20-26份。3.根根据权利要求1所述的一种船底高效抗菌涂料，其特征在于，所述抗菌涂料由以下重量份的原料制成：环氧树脂40份、纳米二氧化钛8份、纳米氧化锌10份、N-十二烷基双季铵盐14份、碳酸钙6份、硅藻土4份、硬脂酸锌1.8份、柠檬醛8份、二甲苯23...
【专利技术属性】
技术研发人员：王和山，王厚国，王和东，殷东楼，殷芳荣，曹文强，张万霞，张萍，
申请(专利权)人：安徽开林新材料股份有限公司，
类型：发明
国别省市：安徽,34