The invention discloses a high-strength and heat-resistant wood-plastic composite material and its preparation method. The material comprises 50 60 copies of polyethylene, 5 10 copies of ABS resin, 30 35 copies of plant material, 15 20 copies of high-strength heat-resistant agent, 3 4 copies of coupling agent, 3 4 copies of lubricant and 1 2 copies of mould-proof, of which the high-strength heat-resistant agent is described. For the mixture of diatomite and attapulgite, the mass ratio of diatomite and attapulgite is 1:0.5 1. The invention improves the temperature resistance and mechanical properties of wood-plastic composites by adding a mixture of diatomite and attapulgite as a high-strength heat-resistant agent in wood-plastic composites.
【技术实现步骤摘要】
高强耐温木塑复合材料及其制备方法
本专利技术涉及木塑材料领域，更具体地，涉及一种高强耐温木塑复合材料及其制备方法。
技术介绍
木塑复合板材是一种主要由木材(木纤维素、植物纤维素)为基础材料与热塑性高分子材料(塑料)和加工助剂等，混合均匀后再经模具设备加热挤出成型而制成的高科技绿色环保新型装饰材料，兼有木材和塑料的性能与特征，是能替代木材和塑料的新型复合材料。木塑复合材料作为新型复合材料具有使用寿命长、可塑性强以及环保健康等优点，但是，目前的木塑复合材料存在耐高温性能较差和力学性能不理想的问题，因此有必要提供一种高强耐温木塑复合材料。
技术实现思路
本专利技术的目的是提供一种高强耐温木塑复合材料，通过添加高强耐温剂，提高木塑复合材料的耐温性和力学性能。为了实现上述目的，本专利技术的一方面提供一种高强耐温木塑复合材料，以质量份数计，该材料包括：聚乙烯50-60份，ABS树脂5-10份，植物材料30-35份，高强耐温剂15-20份，偶联剂3-4份，润滑剂3-4份，防霉剂1-2份其中，所述高强耐温剂为硅藻土和凹凸棒土的混合物，所述硅藻土和凹凸棒土的质量比为1:0.5-1。本专...
【技术保护点】
1.一种高强耐温木塑复合材料，其特征在于，以质量份数计，该材料包括：聚乙烯50‑60份，ABS树脂5‑10份，植物材料30‑35份，高强耐温剂15‑20份，偶联剂3‑4份，润滑剂3‑4份，防霉剂1‑2份其中，所述高强耐温剂为硅藻土和凹凸棒土的混合物，所述硅藻土和凹凸棒土的质量比为1:0.5‑1。
【技术特征摘要】
1.一种高强耐温木塑复合材料，其特征在于，以质量份数计，该材料包括：聚乙烯50-60份，ABS树脂5-10份，植物材料30-35份，高强耐温剂15-20份，偶联剂3-4份，润滑剂3-4份，防霉剂1-2份其中，所述高强耐温剂为硅藻土和凹凸棒土的混合物，所述硅藻土和凹凸棒土的质量比为1:0.5-1。2.根据权利要求1所述的高强耐温木塑复合材料，其中，所述聚乙烯为高密度聚乙烯。3.根据权利要求1所述的高强耐温木塑复合材料，其中，所述植物材料为木粉、秸秆粉、稻壳粉和竹粉的混合物。4.根据权利要求3所述的高强耐温木塑复合材料，其中，所述木粉、所述竹粉和所述稻壳粉的质量比为1:(0.5-0.6):(0.2-0.3)：(0.2-0.3)。5.根据权利要求1所述的高强耐温木塑复合材料，其中，所述偶联剂为硅烷偶联剂和/或钛酸酯偶联剂。6.根据权利要求1所述的高强耐温木塑复合材料，其中，所述润滑剂为聚乙烯蜡、石蜡和硬脂酸中的至少一种。7.根据权利要求1所述的高强耐温木塑复合材料，其中，所述防霉剂为五氯苯...
【专利技术属性】
技术研发人员：潘杰，
申请(专利权)人：芜湖瑞祥木业包装有限公司，
类型：发明
国别省市：安徽,34