A marine medium titanium high fluorine melting flux and its preparation method belong to the field of welding technology; the composition of the melting flux is as follows: CaF2:70-80% and titanium 2:20-30% by mass percentage; the total mass percentage of each component is 100%; the preparation method is as follows: 1) According to the proportion of the marine medium titanium high fluorine melting flux, each group is weighed. The raw materials are evenly mixed; the melted products are quenched by water for more than 30 minutes after smelting to produce glass semi-finished products; 2) the glass semi-finished products are roasted at high temperature to produce roasted products; 3) the roasted products are crushed and sifted, and the particles with grain size of 14-110 meshes are ultra-medium titanium and high fluorine melting flux for marine use; and the marine medium titanium and high fluorine flux of the present invention is provided. The tensile strength of the welded joint is 687-715 MPa and the impact energy at low temperature (40 C) is 67-83J.
【技术实现步骤摘要】
一种船用中钛高氟型熔炼焊剂及其制备方法
本专利技术属于焊接
，具体是一种船用中钛高氟型熔炼焊剂及其制备方法。
技术介绍
埋弧焊焊剂是埋弧焊主要的消耗材料之一，在焊接过程中对焊缝金属起机械保护、冶金处理及改善焊接工艺性能的作用，焊剂的焊接工艺性能和化学冶金性能是决定焊缝金属质量的重要因素。相比烧结焊剂，熔炼焊剂具有颗粒均匀高、熔敷金属化学成分均匀、吸潮倾向小、焊接过程稳定、气体烟尘量较少、重复利用率高等优点。中钛高氟型熔炼焊剂氧化性弱，抗气孔能力强，有利于获得高低温韧性的焊缝金属。为满足工业化生产对性能优良的焊剂的紧迫需求，有必要制备一种性能优良、能够实现焊缝金属强度和高的低温韧性，同时具有光滑的焊道，良好脱渣性的钛氟型熔炼焊剂。
技术实现思路
针对现有技术的不足，本专利技术提供了一种船用中钛高氟型熔炼焊剂及其制备方法；本专利技术的熔炼焊剂是一种焊接过程稳定、焊缝金属强度高，低温韧性高，焊缝成分和组织均匀、焊道表面光滑、脱渣性能良好的钛氟型熔炼焊剂，满足船板钢焊接工艺对性能优良的焊剂的紧迫需求。一种船用中钛高氟型熔炼焊剂，其含有成分按质量百分比为：CaF2：70～...
【技术保护点】
1.一种船用中钛高氟型熔炼焊剂，其特征在于，所述熔炼焊剂含有成分按质量百分比为：CaF2：70～80％，TiO2：20～30％；各组分的质量百分比总和为100％。
【技术特征摘要】
1.一种船用中钛高氟型熔炼焊剂，其特征在于，所述熔炼焊剂含有成分按质量百分比为：CaF2：70～80％，TiO2：20～30％；各组分的质量百分比总和为100％。2.根据权利要求1所述的一种船用中钛高氟型熔炼焊剂，其特征在于，所述船用中钛高氟型熔炼焊剂，焊后所得的焊接接头的抗拉强度强度为687～715MPa，低温冲击功(-40℃)为67～83J。3.权利要求1或2所述的船用中钛高氟型熔炼焊剂的制备方法，其特征在于，包括如下步骤：步骤1，熔炼：(1)按船用中钛高氟型熔炼焊剂的配比，秤...