The invention provides a novel two-dimensional black phosphorus nanosheet MoS2 composite solar energy hydrogen production material and its preparation method and application. The two-dimensional black phosphorus nanosheet MoS2 composite solar hydrogen production material is prepared by simple ultrasonic peeling and solvothermal reaction method. The black phosphorus nanosheet MoS2 composite solar hydrogen production material has a typical two-dimensional composite structure. The developed two-dimensional black phosphorus nanosheet MoS2 composite solar hydrogen production material can be effectively applied to the photocatalytic decomposition of water to prepare hydrogen. The two-dimensional black phosphorus nanosheet MoS2 composite solar energy hydrogen production material has the advantages of environmental protection, low cost, visible light response, stability and simple preparation process.
【技术实现步骤摘要】
一种新型二维黑磷纳米片-MoS2复合太阳能制氢材料及其制备方法和应用
本专利技术属于新能源材料领域，尤其是涉及一种新型二维黑磷纳米片-MoS2复合太阳能制氢材料及其应用。
技术介绍
随着科学技术的迅发展，人类美好生活的需要呈现多方面、多层次、多领域的特点，特别对绿色可持续能源的需求与日俱增。当前，人们获取能源的主要方式还是以煤、石油、天然气为主。但是地球上这些化石资源是有限的，且伴随着大规煤、石油等燃料的使用，产生大量的温室气体和有毒有害的氮氧化合物、含硫化合物等，易造成温室效应、酸雨、雾霾、臭氧层空洞等环境问题。当前，寻找和开发清洁可再生能源已然成为目前全世界所关注的焦点。目前氢能源是一种较为理想的清洁能源，氢能源作为燃料有许多特点:(1)来源广泛，氢是自然界中存在最为广泛的元素，大量存在于水中；(2)燃烧值高，约为汽油的3倍；(3)本身无毒性，且不污染环境，燃烧时只产生水，可以循环利用；(4)便于储存和运输。目前，主要的制氢方法有：电解水制氢、化石燃料制氢、生物制氢、催化分解碳氢化合物制氢、光催化分解水制氢等。其中，光催化分解水制氢是一种相对比较简单、价廉、清...
【技术保护点】
1.一种新型二维黑磷纳米片‑MoS2复合太阳能制氢材料，其特征在于具有典型的二维结构，尺寸在100‑500nm，其化学通式如下：P/MoS2,其中P与MoS2的质量比为5:1‑1:2；采用以下方法制备得到：(1)以黑磷晶体粉末为原料，以N‑甲基吡咯烷酮反应溶剂在冰浴条件下超声20‑25h制备得到黑磷纳米片；(2)黑磷纳米片在四硫代钼酸铵的N,N‑二甲基甲酰胺(DMF)溶液中在180‑220℃条件下通过溶剂热制备得到二维的黑磷纳米片‑MoS2复合太阳能制氢材料。
【技术特征摘要】
1.一种新型二维黑磷纳米片-MoS2复合太阳能制氢材料，其特征在于具有典型的二维结构，尺寸在100-500nm，其化学通式如下：P/MoS2,其中P与MoS2的质量比为5:1-1:2；采用以下方法制备得到：(1)以黑磷晶体粉末为原料，以N-甲基吡咯烷酮反应溶剂在冰浴条件下超声20-25h制备得到黑磷纳米片；(2)黑磷纳米片在四硫代钼酸铵的N,N-二甲基甲酰胺(DMF)溶...