The invention discloses a preparation method of green Dendrobium candidum ointment nourishing agent. Fresh Dendrobium candidum, cooking wine and water are wet ultrafine comminuted together until the paste is pasty, and the paste should be fine without feeling of sand and gravel. After high temperature cooking, softening and ripening sterilization, the mixture is superfine comminuted by high frequency vibrating rod mill and wet method. In addition, honey was boiled for 40 to 60 minutes, and the ointment was obtained. The preparation method is simple and convenient for operation and use.
【技术实现步骤摘要】
绿色铁皮石斛膏滋剂的制备方法
本专利技术涉及膏滋剂领域,具体涉及绿色铁皮石斛膏滋剂的制备方法。
技术介绍
铁皮石斛:茎直立,圆柱形,长9-35厘米,粗2-4毫米,不分枝,具多节;叶二列,纸质,长圆状披针形,边缘和中肋常带淡紫色。总状花序常从落了叶的老茎上部发出,具2-3朵花;花苞片干膜质,浅白色,卵形,长5-7毫米,萼片和花瓣黄绿色,近相似,长圆状披针形,唇瓣白色,基部具1个绿色或黄色的胼胝体,卵状披针形,比萼片稍短,中部反折。蕊柱黄绿色,长约3毫米,先端两侧各具1个紫点;药帽白色,长卵状三角形,长约2.3毫米,顶端近锐尖并且2裂。花期3-6月。生于海拔达1600米的山地半阴湿的岩石上。主要分布于中国安徽、浙江、福建等地。其茎入药,属补益药中的补阴药:益胃生津,滋阴清热。在铁皮石斛用作膏滋剂时,现有的铁皮石斛的膏滋剂的制备方法所得到的膏滋剂的药效较差,效率较低。
技术实现思路
本专利技术所要解决的技术问题是现有的铁皮石斛用作膏滋剂时,得到的膏滋剂的药效较差,不便于使用,目的在于提供绿色铁皮石斛膏滋剂的制备方法,解决铁皮石斛的制备的问题。本专利技术通过下述技术方案实现:绿色铁皮石斛膏滋剂的制备方法,包括以下步骤:(1)将鲜铁皮石斛、料酒、水适量,一起进行湿法超微粉碎,至膏状,膏状物应细腻无沙砾感;(2)将混合液经过高温蒸煮、软化、熟化灭菌后,采用高频振动棒磨机,湿法进行超微粉碎,使颗粒粉碎细度达到5微米以下;(3)再加蜂蜜熬制40~60分钟,收膏得到膏滋剂。绿色铁皮石斛膏滋剂的制备方法,所述步骤(1)中水刚好没过铁皮石斛,加入的料酒为水的体积的八分之一。绿色铁皮 ...
【技术保护点】
1.绿色铁皮石斛膏滋剂的制备方法,其特征在于,包括以下步骤:(1)将鲜铁皮石斛、料酒、水适量,一起进行湿法超微粉碎,至膏状,膏状物应细腻无沙砾感;(2)将混合液经过高温蒸煮、软化、熟化灭菌后,采用高频振动棒磨机,湿法进行超微粉碎,使颗粒粉碎细度达到5微米以下;(3)再加蜂蜜熬制40~60分钟,收膏得到膏滋剂。
【技术特征摘要】
1.绿色铁皮石斛膏滋剂的制备方法,其特征在于,包括以下步骤:(1)将鲜铁皮石斛、料酒、水适量,一起进行湿法超微粉碎,至膏状,膏状物应细腻无沙砾感;(2)将混合液经过高温蒸煮、软化、熟化灭菌后,采用高频振动棒磨机,湿法进行超微粉碎,使颗粒粉碎细度达到5微米以下;(3)再加蜂蜜熬制40~60分钟,收膏得到膏滋剂。2.根据权利要求1所述的绿色铁皮石斛膏滋剂的制备方法,其特征在于,所述步骤...
【专利技术属性】
技术研发人员:高庆凌,
申请(专利权)人:泸州德高生物科技有限公司,
类型:发明
国别省市:四川,51