The invention relates to an environment-friendly reflective building thermal insulation coating, which comprises 15 parts of polyacrylate emulsion, 25 parts of barium sulfate 10, 20 parts of talcum powder, 10 15 parts of talcum powder, 1 3 parts of modified ceramic microspheres, 3 3 5 parts of far-infrared ceramic powder, 5 3 parts of silica sol, 3 components of rutile titanium white powder, and ingredients of film forming AIDS. There are 0.5 thickeners, 0.5 dispersants, 0.2 wetting agents, 0.3 defoaming agents and 50 50 60 water. The environmental protection reflective building heat preservation and insulation coating has excellent weatherability, dual effects of heat insulation and reflection, and good heat preservation and insulation effect.
【技术实现步骤摘要】
一种环保反射建筑保温隔热涂料及其制备方法
本专利技术涉及一种环保反射建筑保温隔热涂料及其制备方法，属于建筑保温材料领域。
技术介绍
建筑能耗占人类能源消耗的30％～40％，我国每年新建房屋面积超过所有发达国家每年建成建筑面积的总和，因此提高建筑物保温隔热性有利于节约能源、降低消耗、改善建筑物的使用功能。随着国家建筑节能、环保产业政策的实施，建筑物的节能降耗显得尤为重要。近年来，由于外墙隔热保温技术的发展，建筑墙体隔热保温涂料也逐步由内墙向外墙转变。其中，反射隔热涂料通过选择合适的基料、功能性颜填料及生产工艺来达到增加表面热反射率、减少涂层积热的目的，以此实现隔热降温效果。在基料相同的条件下，作为涂料重要组成部分的颜填料对反射隔热功效起着主导作用。中空玻璃微珠或空心陶瓷微珠是一种由含硅、铝等元素的氧化物经特殊工艺制成的闭孔型薄壁球形颗粒，球体通常为微米级尺寸，其中填充了导热系数较低的空气或惰性气体，因此密度低、导热系数小，能很好地阻缓热能向物体内部传递。此外，玻璃微珠和陶瓷微珠比表面积大，表层材质对各个方向红外线电磁波的反射率极高，可大大提高涂层的反射隔热性能，这些...
【技术保护点】
1.一种环保反射建筑保温隔热涂料，其特征在于：按照重量份计，包括聚丙烯酸酯乳液15‑25份、硫酸钡10‑20份、滑石粉10‑15份、改性陶瓷微球1‑3份，远红外陶瓷粉3‑5份、硅溶胶3‑5份、金红石型钛白粉13‑15份、成膜助剂0.2份、增稠剂0.5份、分散剂0.5份、润湿剂0.2份、消泡剂0.3份、水50‑60份。
【技术特征摘要】
1.一种环保反射建筑保温隔热涂料，其特征在于：按照重量份计，包括聚丙烯酸酯乳液15-25份、硫酸钡10-20份、滑石粉10-15份、改性陶瓷微球1-3份，远红外陶瓷粉3-5份、硅溶胶3-5份、金红石型钛白粉13-15份、成膜助剂0.2份、增稠剂0.5份、分散剂0.5份、润湿剂0.2份、消泡剂0.3份、水50-60份。2.根据权利要求1所述的一种环保反射建筑保温隔热涂料，其特征在于：所述的改性陶瓷微球的制备方法：将20重量份聚乳酸树脂、5重量份可分散胶粉和0.1份的二氧化钛粉末混合均匀，熔化，然后在翻转式混合反应釜内，将陶瓷微球加热到90-95℃，将熔融状态的混合物喷洒在玻化微珠表面，翻转混合25-30分钟。3.根据权利要求1所述的一种环保反射建筑保温隔热涂料，其特征在于：所述的分散剂为聚丙烯酸钠盐。4.根据权利要求1所述的一种环保反射建筑保...
【专利技术属性】
技术研发人员：汪琦，郭元，
申请(专利权)人：芜湖市棠华建材科技有限公司，
类型：发明
国别省市：安徽,34