一种铽铕掺杂的白土催化剂的制备方法技术

本发明专利技术提供了一种铽铕掺杂的白土催化剂的制备方法，包括以下步骤：由活性白土、二丁锡双(1‑硫甘油)、有机硅季铵盐改性水合三醋酸铽、三(二苯甲酰甲基)铁、双三甲基硅基锑，4‑溴苯硼酸新戊二醇、S‑羧乙基异硫脲嗡盐、三(2,2,6,6‑四甲基‑3,5‑庚二酸)铕、组成的混合物放入高速混合机，主轴转速(rpm)：600‑3000，混合1～5h，得到铽铕掺杂的白土催化剂。催化剂的使用寿命比改性前的白土催化剂寿命提高。

Preparation method of terbium europium doped clay catalyst

The invention provides a preparation method of terbium-europium doped clay catalyst, which comprises the following steps: terbium triacetate hydrate modified by active clay, dibutyltin bis (1_thioglycol), organosilicon quaternary ammonium salt, iron tri (diphenylmethyl) iron, bis (trimethylsilyl) antimony, neopentyl bromophenylborate, S_carboxyethyl isothiourea buzz salt. Europium tris (2,2,6,6_tetramethyl_3,5_heptanedioic acid) mixture was put into a high-speed mixer. The spindle speed (rpm): 600_3000, mixed for 1 to 5 hours, and terbium-europium doped clay catalyst was obtained. The life of the catalyst is longer than that of the modified clay catalyst.

【技术实现步骤摘要】
一种铽铕掺杂的白土催化剂的制备方法
本专利技术涉及一种白土催化剂的制备方法，特别是应用于芳烃中脱除微量烯烃的白土催化剂的制备方法。
技术介绍
重整油中通常含有微量的烯烃杂质，这部分烯烃性质活泼，易形成胶质会影响芳烃产品的质量，而且对一些后续加工过程会有不良影响，为了得到合格的化工原料并保证后续工艺的顺利进行，必须将芳烃中的烯烃杂质。白土精制是最早使用的工艺方法，它采用活性白土处理重整油，其中一部分烯烃被活性白土吸附，另外一部分烯烃与重整油中的芳烃发生反应，从而达到从物料中脱除微量烯烃杂质的目的。这种工艺方法较为简单，同时白土的价格低廉，使得白土精制费用较低，而加氢精制和催化精制费用很高。这些独特的优势决定了白土精制成为目前国内石油化工企业最主要的芳烃脱除烯烃的方法.白土催化剂可用于催化裂化，催化重整等工序，如CN1334318一种全白土型高辛烷值催化裂化催化剂的制备，制备出含一定量NaY沸石的晶化产物微球。将晶化产物经离子交换和水热超稳改性处理，得到一种具有优良使用性能的高辛烷值流化催化裂化催化剂。CN1232862一种全白土型流化催化裂化催化剂及其制备方法，其特点是以中径位的原高岭本文档来自技高网...

【技术保护点】
1.一种铽铕掺杂的白土催化剂的制备方法，其特征在于包括以下步骤：按重量份计，由100份活性白土、1‑5份二丁锡双(1‑硫甘油)、0.5‑2份有机硅季铵盐改性水合三醋酸铽、0.01‑0.08份三(二苯甲酰甲基)铁、0.01‑0.08份双三甲基硅基锑，0.1‑0.5份的4‑溴苯硼酸新戊二醇、0.02‑0.06份的S‑羧乙基异硫脲嗡盐、0.004‑0.008份的三(2,2,6,6‑四甲基‑3,5‑庚二酸)铕、组成的混合物放入高速混合机，主轴转速(rpm)：600‑3000，混合1～5h，即得铽铕掺杂的白土催化剂。

【技术特征摘要】
1.一种铽铕掺杂的白土催化剂的制备方法，其特征在于包括以下步骤：按重量份计，由100份活性白土、1-5份二丁锡双(1-硫甘油)、0.5-2份有机硅季铵盐改性水合三醋酸铽、0.01-0.08份三(二苯甲酰甲基)铁、0.01-0.08份双三甲基硅基锑，0.1-0.5份的4-溴苯硼酸新戊二醇、0.02-0...

【专利技术属性】
技术研发人员：王琪宇，
申请(专利权)人：张玲，
类型：发明
国别省市：浙江,33