A metal anticorrosive coating is prepared by mixing dominant fillers, mucosides and diluents evenly. The dominant fillers, which account for 15-20% of the total weight, are evenly ground by mixing nickel, chromium, magnesium, silver, aluminum, iron and ceramic powder, and then by polyethylene chloride, which accounts for 14-18% of the total weight. The finished product was prepared by mixing and diluting the alkene in a paste-like mucosal agent made of tetrahydrofuran or cyclohexanone. It can effectively prevent acid, alkali, salt media and seawater from corrosion, especially suitable for navigation, seaworthiness and oil industry.
【技术实现步骤摘要】
一种金属防腐蚀涂料
本专利技术涉及一种含有金属粉末的、抗腐蚀涂料,特别是一种金属防腐蚀涂料。
技术介绍
有色金属,尤其是黑色金属,在湿度较大的环境中,和与酸、碱、盐类介质频繁接触的情况下,特别是浸泡在海水中时,极易被锈蚀而大大缩短其使用寿命。目前见市的金属防腐蚀涂料虽各种多样,但真正能耐酸、碱、盐类腐蚀和涂覆后长期浸泡在海水中也能有效地防腐的涂料尚未多见。
技术实现思路
本专利技术的目的是要向公众提供一种喷涂在有色金属或者黑色金属物表面上,便可使其具有较强的耐酸、碱、盐类介质腐蚀性能,即使将其浸泡在海水中,也可长期不锈蚀的新型金属防腐蚀涂料。这种新专利技术的金属防腐涂料也是由显性填料、粘膜剂和稀释剂均匀混合后灌装制成,但其显性填料是由镍粉、铬粉、镁粉、银粉、铝粉、铁粉和陶瓷粉均匀混合后研磨至颗粒直径为0.085~0.064毫米的粉末组成,其中的镍粉可增强本防腐涂料的韧性和抗腐蚀力,铬、镁、铝粉也是在其中起增强防腐性能的作用,银粉是为涂料增加光泽,陶瓷粉可增加涂料涂覆在金属表面后的成型膜面的硬度,而铁粉(主要是FeO2)则可增加涂料对金属、尤其是对黑色金属的附着力;其所谓的粘膜剂,是将聚氯乙烯溶于相应溶剂中制成糊状物,例如对高分子的聚氯乙烯,是以四氢呋喃为溶剂,对低分子的聚氯乙烯,则可用环己酮等酮类、脂类或氯代烃类溶剂;将均匀混合研磨好的显性填料按重量4∶3~4的比例与糊状的粘膜剂均匀搅拌混合后,再以天那水为稀释剂调稀搅拌均匀后装罐封存,便制得本新专利技术的金属防腐蚀涂料。将本新专利技术的金属防腐蚀涂料均匀地涂覆在有色金属或黑色金属物的表面上,就等于为其披着了一 ...
【技术保护点】
1.一种金属防腐蚀涂料,它由显性填料、粘膜剂和稀释剂均匀混合 制成,其特征在于:所述的显性填料是由镍粉、铬粉、镁粉、银粉、铝粉、 铁粉和陶瓷粉均匀混合后研磨至颗粒直径为0.85~0.64毫米的粉末组成, 所谓的粘膜剂是将聚氯乙烯溶于四氢呋喃或环己酮中制成糊状,将显性填 料与糊状的粘膜剂按重量4∶3~4的比例均匀搅拌混合后,再以天那水为稀 释剂调稀搅拌均匀后装缸封存; 其配比量为(以重量计,总重量份额之和为100): 显性填料占15~20,粘膜剂占14~18,稀释剂占71~62; 显性填料中,镍粉为3、铬粉为2、镁粉为2~3、银粉为3~5、 铝粉为1、铁粉为2~3、陶瓷粉2~3;粘膜剂中,聚氯乙烯为3~5, 其余为溶剂。
【技术特征摘要】
1.一种金属防腐蚀涂料,它由显性填料、粘膜剂和稀释剂均匀混合制成,其特征在于:所述的显性填料是由镍粉、铬粉、镁粉、银粉、铝粉、铁粉和陶瓷粉均匀混合后研磨至颗粒直径为0.85~0.64毫米的粉末组成,所谓的粘膜剂是将聚氯乙烯溶于四氢呋喃或环己酮中制成糊状,将显性填料与糊状的粘膜剂按重量4∶3~4的比例均...