The invention discloses a modified montmorillonite flame retardant composition for cables and a preparation method thereof. The modified montmorillonite flame retardant composition for cables takes the modified montmorillonite as the main material, combines with flame retardant additives such as nano-active agent, antimony trioxide and ammonium polyphosphate, and has the advantages of high flame retardancy, low cost and low smoke in the combustion process, and should be prepared. When used to prepare rubber, it can not only make the rubber have good flame retardant properties with low smoke, but also bring good mechanical properties to rubber. Moreover, the preparation method of flame retardant is simple, raw material is easy to obtain, and has high popularization and application value.
【技术实现步骤摘要】
电缆用改性蒙脱土阻燃组合物及其制备方法
本专利技术涉及电缆制造领域，具体地，涉及一种电缆用改性蒙脱土阻燃组合物及其制备方法。
技术介绍
电缆通俗来讲就是由一根或多根相互绝缘的导体和外包绝缘保护层制成，将电力或信息从一处传输到另一处的导线。随着经济的快速发展，越来越多的场所需要电缆传递电力或其他信息，因此对电缆的制造也有更严格的要求。电缆的护套是电缆不可缺少的结构部分，起着保护电缆的作用，保证电缆的通电安全，让电缆线芯和水，空气等介质隔绝避免出现漏电现象。树脂是电缆护套制备的主体材料，所以树脂的性质直接决定了制得电缆护套的性质。阻燃剂的分类可根据元素种类分为卤系、有机磷系、及卤磷系、硅系、铝镁系、钼系、硼系、氮系等等。卤系阻燃剂长期以来以其阻燃效率高、用量少、价格低而闻名于世。自从1986年欧洲首先发现含溴体系燃烧产生的产物中含有的多溴二苯醚、四溴双苯并二恶烷及四溴双苯并呋喃等属于致癌物质，含卤阻燃体系一统天下的局面已经受到了严峻的挑战，采用无卤阻燃材料与产品已是大势所趋的事实。现有的无机阻燃剂(硼系，硅系等)虽然具有低毒，抗腐烛性，价廉，燃烧过程中低烟等优点，但是...
【技术保护点】
1.一种电缆用改性蒙脱土阻燃组合物的制备方法，其特征在于，所述制备方法包括以下步骤：(1)将磷酸氢钠和蒙脱土在水中加热混合，然后加入氯化铝，加热回流，得到凝胶状混合物，再将pH调整至8‑13；(2)将凝胶状混合物进行煅烧，粉碎，得到磷酸基‑铝‑掺杂改性的蒙脱土；(3)将改性的蒙脱土、纳米活性剂、三氧化二锑和聚磷酸铵按照比例混合。
【技术特征摘要】
1.一种电缆用改性蒙脱土阻燃组合物的制备方法，其特征在于，所述制备方法包括以下步骤：(1)将磷酸氢钠和蒙脱土在水中加热混合，然后加入氯化铝，加热回流，得到凝胶状混合物，再将pH调整至8-13；(2)将凝胶状混合物进行煅烧，粉碎，得到磷酸基-铝-掺杂改性的蒙脱土；(3)将改性的蒙脱土、纳米活性剂、三氧化二锑和聚磷酸铵按照比例混合。2.根据权利要求1所述的制备方法，其中，改性的蒙脱土、纳米活性剂、三氧化二锑和聚磷酸铵的质量比为10:1-2:1.5-3:2-3。3.根据权利要求2所述的制备方法，其中，步骤(1)中磷酸氢钠、蒙脱土和氯化铝的质量比为3-5:20:2-4。4.根据权利要求2所述的制备方法，其中，步骤(1)中水与蒙脱土的质量比为...
【专利技术属性】
技术研发人员：吴天凤，米春海，何源，周太平，
申请(专利权)人：芜湖航天特种电缆厂股份有限公司，
类型：发明
国别省市：安徽,34