The invention provides a sprayed and brushing sealant and a preparation method thereof. The sealant provided by the invention comprises 60-120 phr silane modified polyurethane, 20-60 phr aromatic solvent oil, 20-40 phr plasticizer, 1-10 phr silane dehydrating agent, 1-10 phr silane coupling agent, 0.1-6 phr chelating tin catalyst, 0.5-10 phr thixotropic agent, 80.5-185 phr phr filler, 0.1-3 phr anti-ultraviolet agent and 0.1-3 phr light stability. The silane modified polyurethane is selected from one or more of polyurethanes whose terminal group is trimethoxymethylsilane and whose terminal group is methyldimethoxymethylsilane. The sealant can be sprayed and brushed by combining the above specific components and matching them in a specific proportion.
【技术实现步骤摘要】
一种可喷涂可涂刷密封胶及其制备方法
本专利技术涉及密封胶
，特别涉及一种可喷涂可涂刷密封胶及其制备方法。
技术介绍
密封胶是具有一定粘结性的密封材料，用来填充构形间隙，以起到密封作用，其通常还具有防泄漏、防水、防振动及隔音、隔热等作用。随着建筑内饰装潢行业的发展，对密封胶的性能要求也越来越高，目前，许多建筑内饰家具的密封料要求具有可喷涂、可涂刷、环保、可涂饰性等各种性能。聚氨酯密封胶是密封胶领域中的一类代表，然而，若要使聚氨酯密封胶具有可喷涂性能，需要降低其粘度，通常做法是加入溶剂油，然而，加入溶剂油后又会导致整体密封胶的触变性变差，从而导致密封胶不可涂刷。由于密封胶的粘度、触变性、剪切性等特性均会影响产品的可喷涂性和涂刷性，且这些特性之间也会相互交错影响，难以平衡，因此，可喷涂性和可涂刷性往往难以兼得，使得密封胶的配方设计十分困难。故现有聚氨酯密封胶通常还不能兼具可喷涂性和可涂刷性，业内也通常分为喷涂专用密封胶和涂刷专用密封胶，而无法满足既可喷涂又可涂刷的需求。
技术实现思路
有鉴于此，本专利技术的目的在于提供一种可喷涂可涂刷密封胶及其制备方法，本专利技术提供...
【技术保护点】
1.一种可喷涂可涂刷密封胶，其特征在于，包含以下重量份的组分：
【技术特征摘要】
1.一种可喷涂可涂刷密封胶，其特征在于，包含以下重量份的组分：所述硅烷改性聚氨酯选自端基为三甲氧基甲硅烷基的聚氨酯和端基为甲基二甲氧基甲硅烷基的聚氨酯中的一种或几种。2.根据权利要求1所述的密封胶，其特征在于，所述硅烷改性聚氨酯的粘度为10000～55000mPa.s。3.根据权利要求1或2所述的密封胶，其特征在于，所述端基为三甲氧基甲硅烷基的聚氨酯为SPUR-1050聚氨酯和/或SPUR-1015聚氨酯；所述端基为甲基二甲氧基甲硅烷基的聚氨酯为SPUR-1012聚氨酯。4.根据权利要求1所述的密封胶，其特征在于，所述脱芳烃类溶剂油选自D110号溶剂油、D130号溶剂油和RISELLAX409溶剂油中的一种或几种。5.根据权利要求1所述的密封胶，其特征在于，所述增塑剂为邻苯二甲酸二异癸酯。6.根据权利要求1所述的密封胶，其特征在于，所述硅烷脱水剂选自A-171型硅烷脱水剂、VTMO型硅烷脱水剂、乙烯基三甲氧基硅烷脱水剂和氨基硅烷脱水剂中的一种或几...
【专利技术属性】
技术研发人员：刘伟明，陈军，沈峰，陈丹，陶小乐，何永富，
申请(专利权)人：杭州之江新材料有限公司，杭州之江有机硅化工有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。