本发明专利技术是为了解决现有现有化妆品包装材料存在气味大的缺陷，提供一种用于化妆品包装的双层材料及其制备方法，通过自行配制的内外层色母粒子，再加入一定比例的树脂，混合熔融，挤出得到成品。本发明专利技术通过合适的原料及配方，采用本发明专利技术所制定工艺，合成出低气味的产品，可广泛应用于各类化妆品的包装；且该产品无溶剂添加，极大地减少了对环境的污染，也减少对人体的伤害。

Double layer material for cosmetic packaging and preparation method thereof

The present invention aims to solve the defect that the existing cosmetic packaging materials have large odor, and provides a double-layer material for cosmetic packaging and a preparation method thereof. The invention synthesizes low-odor products by adopting suitable raw materials and formulations, adopting the process formulated by the invention, and can be widely used in the packaging of various cosmetics; moreover, the product has no solvent addition, which greatly reduces the pollution to the environment, and also reduces the harm to the human body.

【技术实现步骤摘要】
一种用于化妆品包装的双层材料及其制备方法
本专利技术涉及化妆品
，特别涉及一种用于化妆品包装的双层材料及其制备方法。
技术介绍
随着化妆品行业的快速发展，塑料软管以质量轻、结实耐用、可回收、易于挤取、加工性能及印刷适应性好等特点，受到众多化妆品生产企业的青睐，广泛应用于洁面产品、护肤品和美容美发用品等化妆品的包装中。目前，化妆品包装中常用到的塑料软管存在以下问题：常规配方在经过炮筒加热熔融、螺杆挤出、冷却水喷淋后，会有一定味道残留，在包装化妆品后严重影响化妆品的味道，这样会引起消费者的不适，也极大的影响了用户体验。本专利技术经过配方改良、成型工艺调整，现挤出软管，气味极低，可以忽略不计，很好的解决了现有技术的问题。
技术实现思路
为了克服现有技术的缺陷，本专利技术提供一种用于化妆品包装的双层材料及其制备方法。为了实现上述目的，本专利技术提供以下技术方案：一种用于化妆品包装的双层材料，该产品包含内外两层，所述内层物质中各组分的重量百分比为：树脂40％～60％内层色母3％～5％所述外层物质中的各组分的重量百分比为：树脂40％～60％外层色母5％～10％优选的，所述树脂由低密度聚乙烯(L本文档来自技高网...

【技术保护点】
1.一种用于化妆品包装的双层材料，其特征在于，该产品包含内外两层，所述内层物质中各组分的重量百分比为：树脂      40％～60％内层色母  3％～5％所述外层物质中的各组分的重量百分比为：树脂      40％～60％外层色母  5％～10％。

【技术特征摘要】
1.一种用于化妆品包装的双层材料，其特征在于，该产品包含内外两层，所述内层物质中各组分的重量百分比为：树脂40％～60％内层色母3％～5％所述外层物质中的各组分的重量百分比为：树脂40％～60％外层色母5％～10％。2.根据权利要求1所述的一种用于化妆品包装的双层材料，其特征在于，所述树脂由低密度聚乙烯(LDPE)和线性低密度聚乙烯(LLDPE)组成。3.根据权利要求1所述的一种用于化妆品包装的双层材料，其特征在于，所述内层色母由以下重量百分比的原料组成：4.根据权利要求1所述的一种用于化妆品包装的双层材料，其特征在于，所述外层色母由以下重量百分比的原料组成：5.根据权利要求1所述的一种用于化妆品包装的双层材料，其特征在于，所述内层色母、外层色母的制备方法相同，包括以下步骤：(1)将所有的原料依次加入高速搅拌...