The invention relates to a method for making a three-dimensional graphene ceramic filter plate, which comprises the following steps: 1) adding graphene to acetone solution, stirring evenly, then adding nano-titanium dioxide, and then stirring evenly to obtain a first-grade mixture; 2) adding the first-grade mixture to epoxy resin solution, stirring evenly, and obtaining a second-grade mixture. 3) Removing acetone from the secondary mixture to get the tertiary mixture; 4) Adding the active diluent to the tertiary mixture, stirring evenly, then adding the curing agent, stirring evenly, and then stirring evenly, statically aging to get the graphene coating; 5) Spraying the graphene coating on the surface of porous ceramics or impregnating porous ceramics. In the graphene coating, a graphene coating layer is formed on the surface of the porous ceramics to obtain the semi-finished product of the three-dimensional graphene ceramic filter plate; 6) The semi-finished product of the three-dimensional graphene ceramic filter plate is dried to obtain the finished product of the three-dimensional graphene ceramic filter plate.
【技术实现步骤摘要】
一种三维石墨烯陶瓷过滤板的制作方法
本专利技术涉及过滤板材
,尤其是涉及一种三维石墨烯陶瓷过滤板的制作方法。
技术介绍
多孔陶瓷用作过滤器早有应用,但普通的多孔陶瓷过滤器吸附除污能力并不强。石墨烯是一种单原子厚度的二维蜂窝状结构新型碳材料,由于其独特而奇异的各种性能,如单层石墨烯具有超凡的电子性质、热学、力学性能以及巨大的比表面积(高达2965m2/g)而受到科学家们的广泛关注与研究。特别是石墨烯巨大的比表面积在吸附除污领域具有广阔的应用前景,但二维平面石墨烯吸附能力有限。
技术实现思路
本专利技术的目的在于利用多孔陶瓷具有的三维孔网状结构,提供一种设计合理,制作简单,成本低廉的三维石墨烯陶瓷过滤板的制作方法。为实现上述目的,本专利技术采用以下技术方案:一种三维石墨烯陶瓷过滤板的制作方法,其包括以下步骤:1)按照每毫升丙酮溶液添加石墨烯0.5-1.5mg以及纳米二氧化钛0.05-1.0mg的配比,先将石墨烯加至丙酮溶液中,搅拌均匀后,再加入纳米二氧化钛,继续搅拌均匀,得到一级混料;2)按照一级混料与环氧树脂溶液的体积比为0.5-2%的配比,将一级混料加至环氧树脂 ...
【技术保护点】
1.一种三维石墨烯陶瓷过滤板的制作方法,其特征在于:其包括以下步骤:1)按照每毫升丙酮溶液添加石墨烯0.5‑1.5mg以及纳米二氧化钛0.05‑1.0mg的配比,先将石墨烯加至丙酮溶液中,搅拌均匀后,再加入纳米二氧化钛,继续搅拌均匀,得到一级混料;2)按照一级混料与环氧树脂溶液的体积比为0.5‑2%的配比,将一级混料加至环氧树脂溶液中,搅拌均匀,得到二级混料;3)将二级混料加热除去丙酮,得到三级混料;4)按照每毫升三级混料添加活性稀释剂0.05‑0.2ml以及固化剂0.06‑0.1ml的配比,先将活性稀释剂加至三级混料中,搅拌均匀后,再加入固化剂,继续搅拌均匀,静置熟化,得 ...
【技术特征摘要】
1.一种三维石墨烯陶瓷过滤板的制作方法,其特征在于:其包括以下步骤:1)按照每毫升丙酮溶液添加石墨烯0.5-1.5mg以及纳米二氧化钛0.05-1.0mg的配比,先将石墨烯加至丙酮溶液中,搅拌均匀后,再加入纳米二氧化钛,继续搅拌均匀,得到一级混料;2)按照一级混料与环氧树脂溶液的体积比为0.5-2%的配比,将一级混料加至环氧树脂溶液中,搅拌均匀,得到二级混料;3)将二级混料加热除去丙酮,得到三级混料;4)按照每毫升三级混料添加活性稀释剂0.05-0.2ml以及固化剂0.06-0.1ml的配比,先将活性稀释剂加至三级混料中,搅拌均匀后,再加入固化剂,继续搅拌均匀,静置熟化,得到石墨烯涂料;5)将石墨烯涂料喷涂在多孔陶瓷表面或者将多孔陶瓷浸渍于石墨烯涂料中,以在多孔陶瓷表面形成石墨烯涂料层,得到三维石墨烯陶瓷过滤板半成品;6)将三维石墨烯陶瓷过滤板半成品烘干,得到三维石墨烯陶瓷过滤板成品。2.根据权利要求1所述的一种三维石墨烯陶瓷过滤板的制作方法,其特征在于:步骤3)中加热的温度为60-70℃。3.根据权利要求1所述的一种三维石墨烯陶瓷过滤板的制作方法,其特征在于:步骤4)中活性稀释剂为缩水甘油醚...