The invention discloses a hydrophobic cable material, which is composed of the following weight components of raw materials: trifluoroethyl methacrylate 36_40, acetic anhydride 2_4, sulfuric acid 0.1_0.2 with a concentration of 96_98%, initiator 1_1.2, polyvinyl chloride 110_130, triglyceride octanoate 6_8, organosilicon powder solution 30_40. Silicon powder solution is used as reaction solvent and polymerized under the action of initiator to obtain silicon powder modified polymer, thereby improving the dispersion compatibility of silicon powder between polymer matrix. The fluorinated polymer and silicon powder introduced by the invention effectively improve the hydrophobic property of the surface of the finished product.
【技术实现步骤摘要】
一种疏水电缆料及其制备方法
本专利技术属于电缆料领域，具体涉及一种疏水电缆料及其制备方法。
技术介绍
随着电缆事业的快速发展，高质量的电缆料受到越来越多的青睐，高质量的电缆料不仅耐候性好，使用寿命长，而且安全环保，因此追求更高质量的电缆料不仅可以赢得市场的竞争，还对现代化建设起到了重大的支持和帮助；在多雨潮湿地区，电缆长期浸泡在水中，容易造成起泡、开裂等现象，从而影响电缆的正常使用。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种疏水电缆料及其制备方法。为实现上述目的，本专利技术采用以下技术方案：一种疏水电缆料，它是由下述重量份的原料组成的：甲基丙烯酸三氟乙酯36-40、乙酸酐2-4、浓度为96-98%的硫酸0.1-0.2、引发剂1-1.2、聚氯乙烯110-130、辛酸癸酸三甘油酯6-8、有机硅微粉溶液30-40。所述的引发剂为过硫酸铵、过硫酸钠中的一种。所述的有机硅微粉溶液是由下述重量份的原料组成的：硅微粉10-20、硬脂酸钙2-3、n-水杨酰苯胺5-7、10-12%的甲醛水溶液2-3、羧甲基纤维素钠0.1-0.4。所述有机硅微粉溶液的制备方法...
【技术保护点】
1.一种疏水电缆料，其特征在于，它是由下述重量份的原料组成的：甲基丙烯酸三氟乙酯36‑40、乙酸酐2‑4、浓度为96‑98%的硫酸0.1‑0.2、引发剂1‑1.2、聚氯乙烯110‑130、辛酸癸酸三甘油酯6‑8、有机硅微粉溶液30‑40。
【技术特征摘要】
1.一种疏水电缆料，其特征在于，它是由下述重量份的原料组成的：甲基丙烯酸三氟乙酯36-40、乙酸酐2-4、浓度为96-98%的硫酸0.1-0.2、引发剂1-1.2、聚氯乙烯110-130、辛酸癸酸三甘油酯6-8、有机硅微粉溶液30-40。2.根据权利要求1所述的一种疏水电缆料，其特征在于，所述的引发剂为过硫酸铵、过硫酸钠中的一种。3.根据权利要求1所述的一种疏水电缆料，其特征在于，所述的有机硅微粉溶液是由下述重量份的原料组成的：硅微粉10-20、硬脂酸钙2-3、n-水杨酰苯胺5-7、10-12%的甲醛水溶液2-3、羧甲基纤维素钠0.1-0.4。4.根据权利要求3所述的一种疏水电缆料，其特征在于，所述有机硅微粉溶液的制备方法，包括以下步骤：（1）取n-水杨酰苯胺，加入到其重量10-17倍的无水乙醇中，搅拌均匀，加入硬脂酸钙，升高温度为60-65℃，保温搅拌20-30分钟，加入硅微粉，保温搅拌1-2小时，得苯胺醇溶液；（2）取羧甲基纤维素钠，加入到其重量50-70...
【专利技术属性】
技术研发人员：方万漂，
申请(专利权)人：温州市赢创新材料技术有限公司，
类型：发明
国别省市：浙江,33