The invention discloses a cobalt-manganese doped tin dioxide nanotube and a preparation method thereof. In the invention, a certain amount of manganese acetate, cobalt acetate and dibutyltin oxalate are dissolved in a certain volume of N, N_dimethylformamide and ethanol, and then a suitable amount of polyvinylpyrrolidone is added and stirred to obtain a brown-red precursor mixture. The electrospun products were sintered to form cobalt manganese doped tin dioxide nanotubes. The electrochemical experiments show that the cobalt-manganese-doped tin dioxide nanotubes prepared by this method have broad application prospects as anode materials for lithium-ion batteries. In the whole preparation process, the operation is simple, the raw material cost is low, the equipment investment is few, and it is suitable for mass production.
【技术实现步骤摘要】
一种掺杂钴、锰二氧化锡纳米管及其制备方法
本专利技术属于材料化学领域，具体涉及到一种掺杂钴锰SnO2纳米管及其制备方法。
技术介绍
与宏观材料相比，纳米结构电极材料比表面积大，能够缩短电子、离子的传输距离，增加电极/电解液界面的面积和反应位点，特别是可缓冲充放电过程中体积变化所产生的内应力，进而提高电极材料的循环稳定性。因此，纳米材料是发展高性能锂离子电池材料的有效途径(梁初等，锂离子电池负极储锂材料的研究进展,2015,29(6):9-10；NamKT等,Science,2006,312(5775):885-888)。SnO2纳米材料作为储锂材料具有理论容量高、能量密度大、原料来源广泛及价格低廉的优点，改善SnO2的比表面积有利于缓冲其充放电过程中的体积变化，同时比表面效应有利于更多的锂发生脱嵌，是一种非常有潜力的锂电负极材料(IdotaY等，Science,1997,276,1395-1397；BesenhardJO等，JournalofPowerSources,1997,68(1):87-90)。2017年邵婷婷等人通过用水热法制备了二氧化锡纳米材料(一种二...
【技术保护点】
1.一种掺杂钴、锰二氧化锡纳米管，其特征在于，该纳米管元素组成化学式为Co0.25Mn0.25Sn0.5O2；所述纳米管的制备方法包括以下步骤：1)称取一定量的醋酸锰，醋酸钴，乙二酸二丁基锡溶于一定体积的N,N‑二甲基甲酰胺和乙醇中，然后加入适量的PVP，搅拌14～16h，得到棕红色的前驱体混合物溶液，混合物溶液中金属元素的摩尔比为Co：Mn：Sn＝1：1：2；2)将得到的棕红色的前驱体混合物溶液在18～20kv电压和0.7～0.9mL/h流率下、相对湿度为35～45％的氛围下进行静电纺丝；3)将得到的静电纺丝产品置于坩埚内，然后将坩埚放置于马弗炉中650～700℃烧结2～...
【技术特征摘要】
1.一种掺杂钴、锰二氧化锡纳米管，其特征在于，该纳米管元素组成化学式为Co0.25Mn0.25Sn0.5O2；所述纳米管的制备方法包括以下步骤：1)称取一定量的醋酸锰，醋酸钴，乙二酸二丁基锡溶于一定体积的N,N-二甲基甲酰胺和乙醇中，然后加入适量的PVP，搅拌14～16h，得到棕红色的前驱体混合物溶液，混合物溶液中金属元素的摩尔比为Co：Mn：Sn＝1：1：2；2)将得到的棕红色的前驱体混合物溶液在18～20kv电...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。